The work deals with the preparation and study of polyphosphate composites. Aluminum phosphates provide some unusual properties like high-heat resistance in terms of inorganic binders. The addition of chromium in the form of Cr2O3 or directly the bond with the aluminum-chromium-phosphate can improve the properties of this binder. Highly viscous Al2Cr(H2PO4)9 and Al3Cr(H2PO4)12 binders were prepared by dissolving Al(OH)3 and CrO3 in 85% phosphoric acid, and mixed with Al2O3 and Cr2O3 fillers. The composites were cured in the furnace at 150 °C for 24 h under pressure of 10 MPa. During the annealing at temperatures up to 1 500 °C changes in chemical structure of the cured composites were observed, leading to the understanding of the creation of crystalline phases and their eventual changes. The characterization of binders was mainly based on FT-IR, EDAX, TG-DTA and optical microscopy analyses.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:216349 |
| Date | January 2008 |
| Creators | Kalina, Lukáš |
| Contributors | Ptáček, Petr, Šoukal, František |
| Publisher | Vysoké učení technické v Brně. Fakulta chemická |
| Source Sets | Czech ETDs |
| Language | Czech |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.1539 seconds