Combustion characteristics of steam-exploded biomass pellets

Currently pelletized woody biomass is widely used as a fuel in thermal applications toaccelerate the global transition to renewable energy. Fuel upgrade is one of the key factorsto improve energy conversion processes. Woody biomass can be fractionated into its mainconstituents by steam explosion. Steam-exploded biomass exhibits enhanced heating valueand improves pellet durability. Moreover, there is a significant deviation in thermochemicalbehavior of steam exploded (steam-treated) biomass with respect to the raw material duringpyrolysis. This thesis work concerned combustion characteristics of steam-exploded salix. The steamtreatedmaterial was pelletized and combusted under 21% of oxygen with varying thereactor temperature from 500 to 900°C to study the influence of both surrounding andpretreatment conditions during combustion process. The impact of different pretreatmentseverity factors (Ro) on burning behavior was evaluated: mild (205°C-6min, Ro=3.87),intermediate (205°C-12min, Ro=4.17) and severe (228°C-12min, Ro=4.84). Heterogeneousand homogenous ignition mechanisms were observed, which were dependent on the reactortemperature. The ignition time and devolatilization duration were observed independent onpretreatment severity near 900°C, and slightly influenced near 500°C. Enhanceddevolatilization rate was detected with the increment of Ro from 3.87 to 4.17, whilst themost severe pretreatment conditions (Ro=4.84) weakened biomass reactivity duringdevolatilization. Finally, char reactivity was lowered as a result of the increment ofpretreatment severity.

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kth-36199
Date January 2011
CreatorsPonce Valle, Maria Gabriela
PublisherKTH, Energi- och ugnsteknik
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeStudent thesis, info:eu-repo/semantics/bachelorThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0016 seconds