Orientador: Alexandre Augusto Zaia / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-08T12:23:42Z (GMT). No. of bitstreams: 1
Moreira_DannaMota_M.pdf: 5878321 bytes, checksum: 4089eb0ec4e19d31fd9966e0b4a6b16f (MD5)
Previous issue date: 2007 / Resumo: O objetivo desse trabalho foi avaliar a ocorrência de alterações na estrutura e organização do colágeno presente na matriz orgânica da parede dentinária do canal radicular de incisivos bovinos bem como, avaliar a topografia da matriz inorgânica desta estrutura após irrigação com hipoclorito de sódio 5,25%, EDTA 17% e clorexidina gel 2%. Foram utilizados 60 dentes bovinos divididos aleatoriamente em seis grupos com 10 dentes cada: G1 - Hipoclorito de sódio (NaOCl) 5,25% e EDTA 17%; G2 - Clorexidina gel 2%; G3 - NaOCl 5,25%; G4 - EDTA 17%; G5 - Clorexidina gel 2% e EDTA 17%; G6 - Solução de cloreto de sódio 0,9% (Controle). Uma análise paralela foi realizada em 10 dentes onde nenhum tipo de procedimento foi realizado, sendo possível a obtenção dos parâmetros da birrefringência característica de incisivos bovinos sem instrumentação. As amostras experimentais foram submetidas à instrumentação e irrigação com as diferentes substâncias químicas auxiliares e em seguida, segmentadas em dois fragmentos. Um fragmento foi processado histologicamente utilizando o corante pricrosirius e em seguida, seu retardo óptico foi mensurado por meio de microscopia de polarização. O outro segmento foi preparado e avaliado por meio de microscopia eletrônica de varredura. Os resultados das mensurações dos retardos ópticos foram submetidos à análise estatística por meio do teste de Dunnet. Os resultados demonstraram que os grupos tratados com a clorexidina gel 2% e EDTA 17%, associados ou não, não obtiveram diferença estatisticamente significante em relação ao grupo controle. Nos grupos tratados com NaOCl 5,25%, associado ou não ao EDTA 17%, as médias dos retardos ópticos foram estatisticamente diferentes ao grupo controle. Concluindo que o NaOCl 5,25% provoca alterações na organização macromolecular do colágeno presente na matriz orgânica da dentina radicular de dentes bovinos. A análise realizada por meio da MEV demonstrou alterações estruturais na matriz inorgânica em todos os grupos em que o EDTA 17% foi utilizado / Abstract: The aim of this study was to evaluate the change in collagen structure and organization present in the organic matrix of the dentine wall of the root canals of bovine inferior incisors as well as the topography of the inorganic matrix after irrigation with 5.25% sodium hypochlorite, 17% EDTA and 2% chlorexidine gel. Sixty bovine incisors were randomly divided into six groups of 10: G1 - 5.25% Sodium Hypochlorite (NaOCl) and 17% EDTA; G2 - 2% Chlorexidine gel; G3 - 5.25% NaOCl; G4 - 17% EDTA; G5 - 2% Chlorexidine gel and 17% EDTA; G6 (Control) - 0.9% Sodium chloride. A parallel analysis was performed with 10 teeth which had not been submitted to any treatment. Hence, it was possible to obtain parameters for the birefringence characteristic of non-instrumented inferior bovine incisors. Experimental samples were submitted to instrumentation and irrigation with different auxiliary chemical substances and then segmented in two. One fragment was histologically processed using picrosirius pigment. Its optical retardations were measured through polarization microscopy. The second fragment was prepared to be evaluated through scanning electron microscopy. The optic retardation measurement data were submitted to statistical analysis using Dunnet?s test. Results revealed that the groups that associated or not 2% chlorexidine gel and 17% EDTA were not statistically different in relation to the control group. For the groups which 5.25% NaOCl was used, associated or not to 17% EDTA, the average optic retardations were statistically different to the control group. Therefore, 5.25% sodium hypochlorite proved to cause alterations to the molecular organization of collagen present in the organic matrix of root dentine of bovine teeth. Scanning electron microscopy showed structural alterations of the inorganic matrix of all groups tested with 17% EDTA / Mestrado / Endodontia / Mestre em Clínica Odontológica
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289846 |
Date | 16 February 2007 |
Creators | Moreira, Danna Mota |
Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Záia, Alexandre Augusto, 1968-, Filho, Eduardo Diogo Gurgel, Souza Filho, Francisco José de |
Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | 77p. : il., application/pdf |
Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0019 seconds