Filmes Langmuir-Blodgett de poliuretanos funcionalizados com azobenzenos e suas propriedades de armazenamento óptico / Langmuir-Blodgett films of functionalized polyurethanes and their optical storage properties

Neste trabalho foram feitas as sínteses de dois poliuretanos utilizando-se o corante DR19 (4-(bis-N-2-hidroxietil)amino-4\'-nitroazobenzeno), o DR19MDI-PU derivado do 4,4\' difenilmetano-diisocianato e o DR19IPDI-PU derivado diisocianato de isofurona. O corante foi sintetizado e caracterizado por espectroscopia na região do infravermelho (FTIR), espectroscopia na região do ultravioleta visível (UV-Vis) e ressonância magnética nuclear de próton (HRMN). Os polímeros foram caracterizados por FTIR, UV-Vis, termogravimetria e calorimetria diferencial de varredura. As massas molares, Mn e Mw, e a polidispersividade foram determinadas por cromatografia de exclusão por tamanho. Um estudo sistemático foi realizado sobre as propriedades dos filmes de Langmuir destes polímeros. Monocamadas do DR19IPDI-PU puro apresentaram uma área maior por monômero, ao contrário do esperado porque sua unidade repetitiva é menor do que a do DR19MDI-PU. Entretanto, nos filmes mistos com estearato de cádmio (CdSt), na razão de 50:50% em massa, a área foi essencialmente a mesma para os dois polímeros, o que foi atribuído à influência do CdSt na agregação das macromoléculas. Isto foi confirmado pela forte interação entre CdSt e DR19MDI-PU que fez com que o potencial de superfície do filme misto fosse maior do que o dos filmes dos componentes puros. Apesar de os filmes de Langmuir dos polímeros puros serem estáveis, eles não eram passíveis de transferência para substratos sólidos, e por isso filmes Langmuir-Blodgett (LB) foram produzidos a partir dos filmes mistos com CdSt. Os filmes fabricados eram do tipo Y, com taxa de transferência próxima de 1. Medidas de espectroscopia óptica comprovaram a existência do CdSt e dos polímeros nos filmes LB e que a quantidade de material transferida em cada deposição foi a mesma. A agregação também afetou as propriedades dos filmes LB mistos, com os filmes de DR19MDI-PUICdSt apresentando um espectro UV-vis. característico de agregação do tipo H, ao contrário do caso de filmes LB de outros azopolímeros, incluindo o DR19IPDI-PU. Nos filmes LB, os domínios de CdSt e do polímero estão separados, como indicado por medidas de difração de Raios X, que mostraram picos de Bragg intensos característicos de estruturas com um espaçamento de bicamadas muito próximo do valor encontrado para filmes de CdSt puro. A fotoisomerização dos filmes LB foi investigada realizando-se ciclos de escrita-apagamento do processo de armazenamento óptico. A birrefringência induzida opticamente é estável, podendo ser eliminada com luz kircularmente polarizada. Ela aumenta com a potência do laser de escrita, antes de atingir a saturação. A potência de saturação é maior para o DR19MDIPU, provavelmente devido à agregação nestes filmes. Efeitos de agregação foram comprovados a partir de comparações dos resultados dos filmes LB com filmes obtidos por centrifugação dos polímeros investigados. A birrefringência máxima nos filmes LB diminui com o número de camadas depositadas porque o grau de ordenamento diminui quando um grande número de camadas é depositado, analogamente ao observado em filmes LB e de outros azopolímeros / Two polyurethanes have been synthesized with the functionalization with azobenzene dye, namely DR19 (4-(bis-N-2-hydroxyethyl)amino-4\'-nitroazobenzene). The dye was also synthesized as part of the work, and its structure was confirmed by infrared spectroscopy (FTIR), Ultraviolet visible spectroscopy (UV-Vis) and proton nuclear magnetic resonance (H-RMN). The resultant polymers, DR19IPDI-PU and DR19MDIPU, were characterized by FTIR, Uv-Vis providing results as expected from the anticipated molecular structures. Their molecular weights, Mn and Mw, and their polydispersity were determined by size-exclusion chromatography. Thermogravimetry and differential scanning calorimetry were also employed. A systematic investigation was carried out on the monolayer properties of these polymers. While monolayers of pure DR19MDI-PU displayed a larger area per repeat unit, contrary to expected as its unit is smaller than DR19IPDI-PU, their mixed monolayers with cadmium stearate (CdSt) (50:50% in weight) had the same area as the mixed monolayers of DR19IPDIPU. This was attributed to the influence of CdSt on the aggregation of DR19MDI-PUmacromolecules, which was confirmed by the strong interaction between CdSt and DR19MDI-PU that led to a monolayer surface potential for the mixed monolayer which was higher than for the value of both separate components. Eventhoughthe Langmuir monolayers of the pure polymers were stable at the airlwater interface, their b transferability was poor and therefore Langmuir-Blodgett (LB) films were produced from the mixed monolayers with CdSt, leading to Y-type films with near unity transfer ratios. Optical spectroscopy measurements confirmed the presence of CdSt as well as the polymer in the LB films, and also that the amount of material deposited in each transfer step was the same. Aggregation also played an important role in the properties of the transferred mixed LB films, as films from DR19MDI-PUICdSt displayed a UV-vis. spectrum characteristic of H-aggregates, unlike the case of LB films from other azobenzene-containing polymers, including DR19IPDI-PU. In the LB films, the domains of CdSt and polymer appear separately, as indicated by X-ray diffraction which showed intensive Bragg peaks which were characteristic of structures with a bilayer thickness very close to that of pure CdSt films. Photoisomerization of the LB films was investigated by performing writing-erasing cycles of optical storage processes. The photoinduced birefringence was stable, and could be eliminated by impinging circularly polarized light on the film. It increased with the power of the writing laser before reaching saturation. The power for saturation was higher for DR19MDI-PU, probably due to the aggregation of these films. Effects from aggregation were confirmed uponcomparing data for LB films with those from spin-coated films of the polymers investigated. The maximumbirefringence in the LB films decreased with the number of layers because the degree of order decreases as a large number of layers are deposited, similarly to the observed with LB films of other azobenzene-containing polymers

Identiferoai:union.ndltd.org:IBICT/oai:teses.usp.br:tde-18112014-161756
Date09 November 2000
CreatorsDavid Sotero dos Santos Junior
ContributorsOsvaldo Novais de Oliveira Junior, Jose Luis Cardozo Fonseca, Adhemar Colla Ruvolo Filho
PublisherUniversidade de São Paulo, Ciência e Engenharia de Materiais, USP, BR
Source SetsIBICT Brazilian ETDs
LanguagePortuguese
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis
Sourcereponame:Biblioteca Digital de Teses e Dissertações da USP, instname:Universidade de São Paulo, instacron:USP
Rightsinfo:eu-repo/semantics/openAccess

Page generated in 0.0029 seconds