The behavior of 8-harness satin woven Celion 3000/PMR-15 graphite-polyimide was experimentally investigated. Unnotched and center-notched specimens from (0)₁₅, (0)₂₂, and (0,45,0, - 45,0,0, - 45,0,45,0)₂ laminates were tested. Material properties were measured and damage development documented under monotonic tension, sustained incremental tension, and tension-tension fatigue loading. Damage evaluation techniques included stiffness monitoring, penetrant-enhanced X-ray radiography, laminate deply, and residual strength measurement. Material properties of the woven graphite-polyimide were comparable to those of woven graphite-epoxy. Damage development in woven graphite-polyimide was quite different than in non-woven graphite-epoxy. Matrix cracking was denser and delamination less extensive in the graphite-polyimide material system, and as a result, increases in notched residual tensile strength were much lower. A ply level failure theory was used to successfully predict the notched tensile strength of the (0,45,0, - 45,0,0, - 45,0,45,0)₂ laminate based on experimental data from the (0)₂₂ laminate. A simple method was used to simulate fatigue damage in a (0)₂₂ notched specimen to predict residual strength as a function of fatigue life. The advantages and disadvantages of the ply level failure theory used in this study are discussed. / Master of Science
| Identifer | oai:union.ndltd.org:VTETD/oai:vtechworks.lib.vt.edu:10919/43831 |
| Date | 21 July 2010 |
| Creators | Wagnecz, Linda |
| Contributors | Engineering Mechanics |
| Publisher | Virginia Tech |
| Source Sets | Virginia Tech Theses and Dissertation |
| Detected Language | English |
| Type | Thesis, Text |
| Format | xi, 154 leaves, BTD, application/pdf, application/pdf |
| Rights | In Copyright, http://rightsstatements.org/vocab/InC/1.0/ |
| Relation | OCLC# 16796324, LD5655.V855_1987.W335.pdf |
Page generated in 0.0022 seconds