Alkali activated materials, especially when activated with waterglass, are subjected to substantial drying shrinkage that hinders their broader industrial application. The effect of shrinkage reducing admixtures (SRA), based on poly(propylene glycol), on drying shrinkage of alkali activated blast furnace slag (BFS) mortars was studied. The aim of this thesis is to determine the efficiency of SRA as well as the influence of different type of alkali activator with varying silicate modulus on drying shrinkage characteristics. It was observed that the high amount of alkalis positively influenced the effect of SRA. The higher the amount of alkalis, the lower the drying shrinkage was. It also caused more water to be incorporated in the alkali activated structure and prevent it from evaporation. Thus, the weight change of such mortars was the lowest. Reduced effect of SRA on mechanical strength properties was observed in mortars with low amount of alkalis which was connected with delayed hydration resulting in insufficient amount of created C-S-H gel. The presented thesis further discussed and underlines the role of different kinds of alkali ions as well as their amount on the properties of alkali activated BFS systems.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:295652 |
Date | January 2017 |
Creators | Vašíčková, Kateřina |
Contributors | Bílek, Vlastimil, Kalina, Lukáš |
Publisher | Vysoké učení technické v Brně. Fakulta chemická |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0011 seconds