Orientador: Frederico Andrade e Silva / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-07-23T01:30:39Z (GMT). No. of bitstreams: 1
Figueiro_Claudio_M.pdf: 4596354 bytes, checksum: 8f47d3233a23e932d54fe693033e5c6f (MD5)
Previous issue date: 1997 / Resumo: Este estudo avaliou a influência da convergência axial na adaptação e infiltração marginal de coroas totais fixadas com cimentos de fosfato de zinco (S.S. White), ionômero de vidro (Vitremer) e resinoso (Panavia 2 hx). Foram realizados preparos padronizados do tipo coroa total em 60 dentes molares recém extraídos, nos quais foram confeccionadas coroas metálicas em NiCr. Foram formados 12 grupos de acordo com: o agente cimentante utilizado, a convergência axial de 12° e de 16°, e a utilização ou não de ciclagem térmica. As coroas foram cimentadas seguindo as
orientações dos fabricantes, utilizando uma carga estática de 9 Kg durante 7 minutos. Os grupos que sofreram ciclagem térmica foram submetidos a um regime de 1500 ciclos nas temperaturas de 10°C e de 50°C. Todos os grupos foram imersos em corante azul de metileno a 1 %, permanecendo em temperatura de 37°C durante 24 h. As coroas foram seccionadas longitudinalmente utilizando um disco de aço diamantado. Foi efetuado polimento de todas as secções obtidas em uma politriz manual: A adaptação e a infiltração foram medidas utilizando um microscópio comparador (LEITZ), com um
aumento de 40x. Os resultados foram agrupados, e suas médias submetidas a uma análise de variância (com um critério de classificação). O resultado da análise de variância mostrou-se significante ao nível de 5%, sendo realizado o teste
de Tukey ao nível de 5% de significância. Concluiu-se que: I)A Adaptação das coroas foi melhorada com o aumento da convergência, para os cimentos de ionômero de vidro e resinoso. 2) A ordem de classificação dos agentes cimentantes avaliados quanto à adaptação foi: fosfato de zinco, ionômero de vidro, resinoso, da maior para a menor discrepância. 3) A infiltração não sofreu alteração em relação ao grau de convergência das paredes axiais. 4) O cimento resinoso apresentou a
menor infiltração entre os agentes cimentantes avaliados, sendo que os cimentos de fosfato de zinco e ionômero de vidro não apresentaram diferença em relação à infiltração. 5) A utilização da ciclagem térmica aumentou a infiltração, contudo não alterou a classificação dos agentes cimentantes / Abstract: The objective of this study was to evaluate the influence ofaxial convergence on the marginal adaptation and microleakage of cemented complete crowns with Zinc Phosphate (S. S. WHITE), composite resinglass ionomer hybrid Vitremer Luting (3M) and resin cement Panavia 21 EX (KURARA Y). Sixty recently extracted molars were prepared to receive full cast crowns, standardized preparations were made and the crowns were made in a Ni-Cr alloy. Twelve groups were formed according to: luting agents, axial convergence (12° and 16°) and the utilization or not utilization of thermocycling. The crowns were cemented according to the manufacturer' s instructions, utilizing a 9 Kg static load for seven minutes. The specimens were thermocycled for 1500 cycles (1050°C). All groups were immersed in 1 % Methylen Blue solution at 37°C :f:
2°C for 24 hours. The crowns were sectioned with a diamond disk and polished. The marginal adaptation and microleakage were measured using a microscope with 40X of magnification (LEITZ). The results were submitted to the Analysis of variance (ANOV A). The results of Analysis was significant at the 5% leveI, and the Tukey multiple comparisons test . was applied at the 5% leveI of significance. We concluded: 1) The crown adaptation was improved with the increase of the convergence to the glass ionomer and resin cement. 2) The classification order of the lutings cements evaluated according to adaptation was: zinc phosphate, glass ionomer, and resin cement, from the highest to the lowest discrepancy. 3) The convergence angle didn't change the microleakage. 4) The resin cement showed less microleakage than the other luting agent groups. The
microleakage was comparable to zinc phosphate and glass ionomet<. 5) The termocycling increased the microleakage but It didn't change the rank of the luting cements to the microleakage / Mestrado / Protese / Mestre em Clínica Odontológica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289082 |
| Date | 05 December 1997 |
| Creators | Figueiro, Claudio |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Silva, Frederico Andrade e, 1948-, Silva, Wilkens Aurelio Buarque e, Mori, Matsuyoshi |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Clínica Odontológica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 105f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.026 seconds