Resumo: O objetivo desse estudo foi avaliar histológicamente o comportamento de uma membrana experimental, de procedência nacional, membrana de Fluoreto de Polivinilideno-Trifluoreto/CerâmicaTitanato de Bário (PVDF-TrFE/BT) e comparar com os resultados da membrana de colágeno. Para tanto foram confeccionados defeitos ósseos de 6mm de diâmetro em calvária de coelhos. Foram utilizados, um total de 30 coelhos, adultos machos, divididos em quarto grupos: Grupo I: cavidade cirúrgica confeccionada no lado direito da calota craniana do animal, preenchida com osso autógeno e coberta pela membrana experimental de PVDF-TrFE/BT. Grupo II: cavidade cirúrgica confeccionada no lado esquerdo da calota craniana do animal, preenchida com coágulo e coberta pela membrana experimental de PVDF-TrFE/BT. Grupo III: cavidade cirúrgica confeccionada no lado direito da calota craniana do animal, preenchida com osso autógeno e coberta pela membrana de colágeno. Grupo IV: cavidade cirúrgica confeccionada no lado esquerdo da calota craniana do animal, preenchida com coágulo e coberta pela membrana de colágeno. Os animais foram eutanásia nos períodos de 07, 30 e 120 dias. Os espécimes foram tramitados para análise histológica. O grupo I apresentou o melhor resultado em relação à consistência histological do osso neoformado bem como acelerou o processo. Nos grupos I e II, a membrana experimental manteve o espaço do defeito para a reparação óssea. No grupo III e IV, a membrana de colágeno permitiu apenas que houvesse uma reparação parcial da cavidade cirúrgica confeccionada. Por meio dos resultados obtidos, podemos concluir que: a utilização do enxerto ósseo proporcionou a formação de ósseo de melhor consistência com total reparação das cavidades ósseas; a membrana experimental apresentou melhor... (Resumo completo, clicar acesso eletrônico abaixo) / Abstract: The purpose of this study was to histologically evaluate the behavior of a novel membrane of the composite poly(vinylidenetrifluoroethylene)/ barium titane and compare the results with a collagen membrane. The defects were surgically created into the calvarian bone. The study used 30 adult, male rabbits were into from groups follow: Group I - the bone defect of the right side was filled with autogenous bone graft and covered with the novel membrane. Group II - the bone defect of the left side was filled with blood clot and covered with the novel membrane. Group III - the bone defect of the right side was filled with autogenous bone graft and covered with the collagen membrane. Group IV - the bone defect of the left side was filled with blood clot and covered with the collagen membrane. The animals were sacrificed at 07, 30 and 120 days. The results: The group I showed the better bone formation and the accelerated repair. The novel membrane kept the bone space to repair. In the group III and IV, the collagen membrane influenced the bone repair process, so the defects were partial filled by bone. The conclusion: The autogenous bone grafts stimulated the osteogenesis; the novel and the collagen membranes showed biocompatibility and the novel membrane has quality to serve as Bone Gide Regeneration Process; the collagen membrane can be used to cover the grafts or implants materials / Orientador: Marisa Aparecida Cabrini Gabrielli / Coorientador: Valfrido Antonio Pereira Filho / Banca: Eduardo Hochuli Vieira / Banca: Alexandre Elias Trivellato / Mestre
Identifer | oai:union.ndltd.org:UNESP/oai:www.athena.biblioteca.unesp.br:UEP01-000616146 |
Date | January 2010 |
Creators | Santos, André Luiz dos. |
Contributors | Universidade Estadual Paulista "Júlio de Mesquita Filho" Faculdade de Odontologia (Campus de Araraquara). |
Publisher | Araraquara : [s.n.], |
Source Sets | Universidade Estadual Paulista |
Language | Portuguese |
Detected Language | Portuguese |
Type | text |
Format | 103 f. : |
Relation | Sistema requerido: Adobe Acrobat Reader |
Page generated in 0.0021 seconds