This dissertation addresses two critical issues in the mechanical behaviors and structures of bulk-metallic glasses (BMGs): (1) the effect of composition, fabrication method, and pretreatment of plastic deformation on mechanical properties and structures of BMGs; (2) the mechanical response and structural evolution of BMGs in the elastic and plastic region.
(Cu50Zr50)94Al6 and (Cu50Zr50)92Al8 amorphous alloys were used to study the effect of composition on mechanical properties and structures of BMGs. The (Cu50Zr50)94Al6 alloy exhibits lower yield stress and Young’s modulus, higher Poisson’s ratio, worse thermal stability, and better plasticity than (Cu50Zr50)92Al8. Both the topological and chemical effects of Al addition account for the differences of mechanical and physical properties between them.
A Zr55Ni5Al10Cu30 glass-forming alloy with injection casting (the melting temperatures are 1,550 K and 1,250 K, respectively) and with suction casting was fabricated. The results indicate that despite their amorphous structures, the suction-casting samples exhibit a lower yield stress, lower Young’s modulus, and larger plastic strain than the injection-casting samples (the melting temperature is 1,550 K) due to more quenched-in free volumes in suction casting, which results from the higher cooling rate.
The inhomogeneous plastic deformation in Zr50Cu40Al10 BMG samples was introduced by four-point-bend fatigue. There is almost no difference of the stress-strain behaviors between the deformed and undeformed samples. Elastostatic compression was used to introduce homogeneous deformation in Zr70Cu6Ni16Al8 BMG samples. The preloaded samples are softer with decreases of yield strength and Young’s moduli. Anisotropy was observed in the preloaded samples despite their small magnitudes, which even occurred at a relatively low temperature and applied stress level.
The structural evolution of Zr70Cu6Ni16Al8 BMG in the elastic region was analyzed with anisotropic pair density function. The analysis of the first shell of Zr70Cu6Ni16Al8 glass confirms the structural changes in the elastic region. The bond reorientation leads to direction dependent changes in the chemical short-range order. The structural evolution in the plastic region of Zr70Cu6Ni16Al8 BMG is investigated as well. The serrations were observed for both the stress-displacement and full width at half maximum-displacement curves. The excess free volume was measured, which increases with increasing the displacement.
| Identifer | oai:union.ndltd.org:UTENN/oai:trace.tennessee.edu:utk_graddiss-2183 |
| Date | 01 August 2011 |
| Creators | Jiang, Feng |
| Publisher | Trace: Tennessee Research and Creative Exchange |
| Source Sets | University of Tennessee Libraries |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Doctoral Dissertations |
Page generated in 0.0014 seconds