This work has employed the Micro-wave Plasma enhanced Chemical Vapor Deposition (MPCVD) method to fabricate diamond PN junction device. The n+ <111> orientation single-crystal silicon has used as substrates. P-type diamond layer is doped with B(OCH3)3 and the N-type diamond layer is doped with ammonia. The surface structure of diamond film has been observed by scanning electron microscope; and the device rectification property of a PN junction has measured by current-voltage characteristic. The carrier density and mobility of diamond films have been analyzed by Hall measurement. Furthermore, the Cathodoluminescence (CL) spectroscopy showed the defect spectra in diamond PN junction. The N-type diamond film and P-type diamond film have deposited at temperature of 800 ¢J, for 30 minutes and 90 minutes, respectively. The process CVD has performed in the same chamber continually. A I-V curve of sample showed the set on positive voltage 0.5 V and the reverse breakdown voltage of 6 V. Further, CL results revealed a peak at 285 nm (4.4 eV), which represents the CVD diamond band and the other one is at 500 nm (2.5 eV), which stands for donor-acceptor recombination from defect in these diamond films.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0107109-175245 |
| Date | 07 January 2009 |
| Creators | Chen, Hong-Ruei |
| Contributors | none, Tai-Fa Young, none |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0107109-175245 |
| Rights | off_campus_withheld, Copyright information available at source archive |
Page generated in 0.002 seconds