Fabrication and characterization of surface engineered one-dimensional cadmium selenide nanostructure =: (硒化鎘一維納米結構之表面處理及其表徵). / 硒化鎘一維納米結構之表面處理及其表徵 / Fabrication and characterization of surface engineered one-dimensional cadmium selenide nanostructure =: (Xi hua ge yi wei na mi jie gou zhi biao mian chu li ji qi biao zheng). / Xi hua ge yi wei na mi jie gou zhi biao mian chu li ji qi biao zheng

Lam, Ngai Sze. / Thesis (M.Phil.)--Chinese University of Hong Kong, 2008. / Includes bibliographical references. / Text in English; abstracts in English and Chinese. / Lam, Ngai Sze. / Abstract --- p.i / Acknowledgements --- p.iii / Table of contents --- p.iv / List of Figures --- p.viii / List of Tables --- p.xiii / Chapter Chapter 1 --- Introduction --- p.1 / Chapter 1.1 --- Background --- p.1 / Chapter 1.1.1 --- Properties of CdSe --- p.1 / Chapter 1.1.2 --- Synthesis of CdSe one-dimensional (ID) nanostructure --- p.5 / Chapter 1.1.3 --- Application of CdSe nanostructures --- p.8 / Chapter 1.1.4 --- Significance of surface engineering --- p.10 / Chapter 1.1.4.1 --- Surface passivation --- p.11 / Chapter 1.1.4.2 --- Surface functionalization --- p.11 / Chapter 1.1.4.3 --- Modulation of optical/electrical properties --- p.12 / Chapter 1.2 --- Present study --- p.14 / Chapter 1.2.1 --- Objective --- p.14 / Chapter 1.2.2 --- General methodology --- p.14 / Chapter Chapter 2 --- Instrumentation --- p.19 / Chapter 2.1 --- Introduction --- p.19 / Chapter 2.2 --- Setup of Sample Preparation --- p.19 / Chapter 2.2.1 --- Synthesis --- p.19 / Chapter 2.2.1.1 --- Thermal evaporation apparatus --- p.19 / Chapter 2.2.1.2 --- Microwave assisted chemical synthesis --- p.21 / Chapter 2.2.2 --- Sample handling --- p.22 / Chapter 2.2.3 --- Other treatments --- p.22 / Chapter 2.3 --- X-ray photoelectron spectrometer (XPS) --- p.22 / Chapter 2.3.1 --- Basic Principle --- p.22 / Chapter 2.3.2 --- Instrumentation --- p.24 / Chapter 2.3.3 --- Charging problem --- p.27 / Chapter 2.3.4 --- Qualitative analysis --- p.27 / Chapter 2.3.5 --- Quantitative analysis --- p.28 / Chapter 2.3.5.1 --- Curve fitting --- p.28 / Chapter 2.3.5.2 --- Atomic percentage --- p.29 / Chapter 2.3.5.3 --- Thickness determination --- p.29 / Chapter 2.4 --- Photoluminescence --- p.30 / Chapter 2.4.1 --- Basic principle --- p.30 / Chapter 2.4.2 --- Instrumentation --- p.31 / Chapter 2.5 --- Other equipments --- p.32 / Chapter Chapter 3 --- Synthesis of CdSe Nanorods --- p.34 / Chapter 3.1 --- Introduction --- p.34 / Chapter 3.2 --- Thermal evaporation --- p.34 / Chapter 3.2.1 --- Experimental procedures --- p.34 / Chapter 3.2.2 --- Characterization --- p.35 / Chapter 3.3 --- Microwave assisted method --- p.41 / Chapter 3.3.1 --- Experimental procedures --- p.41 / Chapter 3.3.2 --- Characterization --- p.42 / Chapter 3.4 --- Summary --- p.47 / Chapter Chapter 4 --- Surface Treatment of CdSe Nanorods --- p.49 / Chapter 4.1 --- Introduction --- p.49 / Chapter 4.2 --- Experimental procedures --- p.50 / Chapter 4.3 --- Results and Discussion --- p.51 / Chapter 4.3.1 --- Formation of Se-coated CdSe NRs --- p.51 / Chapter 4.3.2 --- Desorption and thinning --- p.56 / Chapter 4.3.3 --- Surface degradation --- p.67 / Chapter 4.4 --- Summary --- p.69 / Chapter Chapter 5 --- Surface Capping of CdSe Nanorods --- p.73 / Chapter 5.1 --- Introduction --- p.73 / Chapter 5.2 --- Experimental procedures --- p.73 / Chapter 5.3 --- Results and Discussion --- p.74 / Chapter 5.3.1 --- Capping of thiol with halo-functional group --- p.74 / Chapter 5.3.1.1 --- Compositional analysis --- p.75 / Chapter 5.3.1.2 --- PL analysis --- p.79 / Chapter 5.3.2 --- Capping of DNA --- p.81 / Chapter 5.3.2.1 --- Compositional analysis --- p.81 / Chapter 5.3.2.2 --- PL analysis --- p.83 / Chapter 5.4 --- Summary --- p.92 / Chapter Chapter 6 --- Conclusions and Future Work --- p.94 / Chapter 6.1 --- Conclusions --- p.94 / Chapter 6.2 --- Future work --- p.95

Identiferoai:union.ndltd.org:cuhk.edu.hk/oai:cuhk-dr:cuhk_326270
Date January 2008
ContributorsLam, Ngai Sze., Chinese University of Hong Kong Graduate School. Division of Materials Science and Engineering.
Source SetsThe Chinese University of Hong Kong
LanguageEnglish, Chinese
Detected LanguageEnglish
TypeText, bibliography
Formatprint, xiii, 96 leaves : ill. ; 30 cm.
RightsUse of this resource is governed by the terms and conditions of the Creative Commons “Attribution-NonCommercial-NoDerivatives 4.0 International” License (http://creativecommons.org/licenses/by-nc-nd/4.0/)

Page generated in 0.0016 seconds