Previous issue date: 2014-08-27 / The longevity of endodontic treatments depends on many variables, including the aging of the filling material and the sealing of the root canal, especially when there is exposure to oral fluids. The aim of this study was to evaluate in vitro the silver nitrate gap penetration in root canals of bovine teeth filled with different endodontic sealers and sealing of the post space preparation with flow resin. The dental crowns of sixty bovine incisors were sectioned and root canals were prepared using a serial technique. The specimens were randomly divided into 6 groups (n= 10 specimens each) according to the root canal sealer used: (AH) AH Plus; (CP) Endo CPM sealer; (EN) Endofill; (RE) RealSeal SE; (SS) AH Plus and post space preparation; (CS) AH Plus and post space preparation and sealing with resin flow. The root canals were filled by lateral condensation using gutta-percha and one of the sealers described above. In groups SS and CS the post space was performed immediately after filling. Ten specimens were randomly selected and the remaining filling was sealed with flow resin. The roots of groups AH, CP, EN and RE, and SS and CS were stored at 100% humidity for 24 months and 24 hours, respectively. After this period, the specimens were immersed in a solution of silver nitrate and prepared for electron microscope (SEM). The areas of filling material-dentin were observed to assess the degree of penetration by silver nitrate. The results show that there were statistically significant differences between the experimental groups AH, CP, EN and RE (p0,05). The sealers AH Plus, Real Seal SE and Endo CPM Sealer showed less infiltration of silver nitrate compared to Endofill (p0,05). Among groups SS and CS, the results showed no statistically significant difference in the penetration of silver nitrate (p > 0.05).
By analyzing the results we can conclude that all root canals showed some degree of gap penetration through the marker silver nitrate. AH Plus, Endo CPM Sealer and RealSeal SE obtained lower gap penetration scores than Endofill. The sealing of the post space preparation with flow resin did not prevent gap formation when compared to the group without sealing. / A longevidade do tratamento endod?ntico est? na depend?ncia de in?meras vari?veis, entre elas o comportamento do material obturador ao longo do tempo e o selamento do canal radicular, especialmente quando da exposi??o aos fluidos bucais. Em face ao acima exposto, o objetivo do presente estudo foi avaliar in vitro a presen?a de gap atrav?s do marcador nitrato de prata, em canais radiculares de dentes bovinos obturados por diferentes cimentos endod?nticos e armazenados por 24 meses, e ap?s o selamento do canal prot?tico com resina flow. Sessenta incisivos bovinos tiveram as coroas dentais seccionadas e os canais radiculares preparados atrav?s da t?cnica seriada. Na sequ?ncia os esp?cimes foram randomicamente divididos em 6 grupos experimentais: (AH) 10 ra?zes obturadas com o cimento AH Plus; (CP) 10 ra?zes obturadas com o cimento Endo CPM-Sealer; (EN) 10 ra?zes obturadas com o cimento Endofill; (RE) 10 ra?zes obturadas com o cimento RealSeal SE; (SS) 10 ra?zes obturadas com o cimento AH Plus e preparo do canal prot?tico; (CS) 10 ra?zes obturadas com o cimento AH Plus, preparo do canal prot?tico e selamento com resina flow. Os canais radiculares foram obturados pela t?cnica da condensa??o lateral utilizando cones de guta-percha e um dos cimentos endod?nticos descritos. Nos grupos SS e CS a desobtura??o parcial do canal radicular foi realizada imediatamente ap?s a conclus?o da obtura??o. Ap?s a realiza??o do preparo do canal prot?tico, 10 esp?cimes escolhidos aleatoriamente tiveram a por??o superficial do remanescente obturador selado com resina do tipo flow. A seguir, a por??o coron?ria de todos os esp?cimes foi selada com cimento restaurador provis?rio e a sa?da foraminal obliterada com cera utilidade. Na sequ?ncia, as ra?zes dos grupos AH, CP, EN e RE, e SS e CS foram armazenadas em umidade 100% por 24 meses e 24 horas, respectivamente. Ap?s esse per?odo os esp?cimes foram imersos em solu??o de nitrato de prata e analisados no microsc?pio eletr?nico de varredura (MEV). As ?reas de uni?o dentina-material obturador foram observadas para avaliar a presen?a de gap marcado por nitrato de prata. Os resultados mostraram que houve diferen?a estatisticamente significativa entre os grupos experimentais AH, CP, EN e RE, quanto ? presen?a de gaps marcados pelo de nitrato de prata (p0,05). Os cimentos AH Plus, Real Seal SE e Endo CPM Sealer apresentaram menor quantidade de gaps marcados pelo nitrato de prata em compara??o ao Endofill (p0,05). J? entre os grupos SS e CS, os resultados mostraram que n?o houve diferen?a estatisticamente significativa em rela??o a presen?a de gaps marcados (p> 0,05).
Ao analisar os resultados pode-se concluir que todos os canais radiculares apresentaram gap marcado por meio do nitrato de prata; os cimentos endod?nticos AH Plus, Endo CPM Sealer e RealSeal SE obtiveram menores escores de gap marcados que o cimento Endofill e o selamento do canal prot?tico com resina flow n?o apresentou menor quantidade de gap marcado quando comparado ao grupo sem selamento.
| Identifer | oai:union.ndltd.org:IBICT/oai:tede2.pucrs.br:tede/1274 |
| Date | 27 August 2014 |
| Creators | Pereira, Charles da Cunha |
| Contributors | Figueiredo, Jos? Antonio Poli de |
| Publisher | Pontif?cia Universidade Cat?lica do Rio Grande do Sul, Programa de P?s-Gradua??o em Odontologia, PUCRS, BR, Faculdade de Odontologia |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da PUC_RS, instname:Pontifícia Universidade Católica do Rio Grande do Sul, instacron:PUC_RS |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -8096554818733665164, 500, 600, 4673435736271820140 |
Page generated in 0.0027 seconds