Condition assessment of existing concrete bridge pier caps using the general shear provisions of the AASHTO LRFD Bridge Design Specification has caused the Georgia Department of Transportation (GDOT) to post a large number of bridges in the State of Georgia. Posting of bridges disrupts the free flow of goods within the region served by the bridge and has a negative economic impact. To prevent structural deterioration, diagonal cracking or failure of concrete pier caps in shear, the GDOT employs an in-situ strengthening technique that utilizes an external vertical post-tensioning system. However, the fundamental mechanics of this system and its effectiveness under service load have not been examined previously.
This research examines the behavior of reinforced concrete pier caps that utilize the above strengthening system in a combined analytical and experimental program. In the experimental part of the study, two groups of full-scale reinforced concrete deep beam specimens were tested. The first group consisted of six deep beams with shear span/depth ratios of approximately 1.0, which is typical of bridge pier caps; of these six, two included the external post-tensioning system. In the second group, nine deep beam specimens that included a segment of the column representing the pier were tested; four of those tests included the external post-tensioning system. The tests revealed that the shear capacity computed using the AASHTO LRFD Bridge Design Specifications provided a conservative estimate of the specimen capacity in all but one case when compared to the experimental results. However, the AASHTO strut and tie provisions were found to provide a much closer assessment of the load carrying mechanism in the pier cap than the general shear provisions, in that they were able to predict the load at which yielding of the tension reinforcement occurred as well as the angle of the compression strut. The presence of the column segment in the second group had a significant impact on the failure mechanism developed in the specimen near ultimate load. The stress concentration at the reentrant corner between the pier cap and column interface served as an attractor for the formation of diagonal shear cracks, a mechanism not observed in previous deep beam tests in shear. The research has led to recommendations for improving the design of pier caps and the external post-tensioning system, where required, based on mechanics which are consistent with the results of the experimental program.
| Identifer | oai:union.ndltd.org:GATECH/oai:smartech.gatech.edu:1853/41076 |
| Date | 17 May 2011 |
| Creators | O'Malley, Curtis John |
| Publisher | Georgia Institute of Technology |
| Source Sets | Georgia Tech Electronic Thesis and Dissertation Archive |
| Detected Language | English |
| Type | Dissertation |
Page generated in 0.0019 seconds