Orientador: Antonio José Ramirez Londono / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Engenharia Mecânica / Made available in DSpace on 2018-08-20T13:37:33Z (GMT). No. of bitstreams: 1
TorresLopez_EdwarAndres_D.pdf: 14707024 bytes, checksum: 982b5dbc99d5f7bbef2ea2c34019eea4 (MD5)
Previous issue date: 2012 / Resumo: Neste trabalho foram realizadas juntas soldadas dissimilares de aço carbono AISI SAE 1020 e a liga de alumínio AA6063-T5, com 2 mm de espessura, empregando o processo de soldagem por atrito com pino não consumível (SAPNC). As juntas soldadas a topo foram realizadas empregando ferramenta de WC-14Co, com diâmetro de ombro e pino de 25,0 e 5,7 mm, respectivamente, e comprimento de pino de 1,35 mm. Foram empregadas velocidades de rotação e avanço de 300 RPM e 150 mm.min-1, respectivamente, para três deslocamentos da ferramenta: +0,5, +1,0 e +1,5 mm. A caracterização microestrutural foi realizada por meio de microscopia óptica e eletrônica de varredura e de transmissão, difração de elétrons retroespalhados (EBSD), espectrometria de raios X dispersiva em energia (X-EDS) e difração de raios X (DRX). Para relacionar os parâmetros de soldagem com a microestrutura das juntas soldadas, foram elaborados os perfis da história térmica durante a soldagem. Juntas soldadas consolidadas foram obtidas para deslocamentos tangenciais da ferramenta (DT) de +1,0 e +1,5 mm, sendo descartado o DT de +0,5 mm por resultarem em penetração heterogênea ao longo da junta. As juntas realizadas no presente trabalho podem ser consideradas como de baixo aporte térmico. Esta condição evitou a formação da denominada zona de menor dureza na zona termicamente afetada (ZTA) do lado do alumínio e de compostos intermetálicos AlxFey na interface alumínio-aço. Na zona misturada, foram obtidas evidências da presença de dois mecanismos de recristalização dinâmica diferentes. No lado de avanço da zona misturada foi identificado o mecanismo de recristalização dinâmica geométrica, enquanto no lado de retrocesso o mecanismo ativo foi recristalização dinâmica continua / Abstract: In this work dissimilar AISI SAE 1020 mild steel and aluminum alloy AA6063-T5 joints, with 2 mm thickness, were friction stir welded (FSW). The welded joints were conducted employing WC-14Co tools, with shoulder and pin diameter of 25.0 and 5.7 mm respectively, and pin length of 1.35 mm. Rotation and weld speeds of 300 RPM and 150 mm.min-1 were employed, for three tool offsets: 0.5, 1.0 and 1.5 mm. The microstructural characterization was performed through optical, scanning and transmission electron microscopy, electron backscatter diffraction (EBSD), energy dispersive X-ray spectroscopy (X-EDS) and x-ray diffraction (DRX). In order to correlate the welding parameters with the final microstructure of the joints, thermal history profiles were collected during welding. Consolidated welded joints were obtained for tool offsets (DT) of +1.0 and +1.5 mm, being discarded the +0.5 mm offset by to produce heterogeneous penetration along the welded joint. The joints made in this work can be considered as low-heat input. This condition prevented the formation of the so-called low hardness zone in heat affected zone (HAZ) aluminum side, and the formation of intermetallic compounds AlxFey in the aluminum-steel interface. In the stir zone evidences of the presence of two different dynamic recrystallization mechanisms were observed. In the advance side of the stir zone, the geometric dynamic recrystallization was identify as working mechanism, while in retreating side of the stir zone, the active mechanism is the so-called continuous dynamic recrystallization / Doutorado / Materiais e Processos de Fabricação / Doutor em Engenharia Mecânica
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/263374 |
| Date | 20 August 2018 |
| Creators | Torres Lopez, Edwar Andres |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Ramirez, Antonio Jose, Londono, Antonio Jose Ramirez, Button, Sergio Tonini, Fogagnolo, João Batista, Franco, Sinésio Domingues, Pinto, Haroldo Cavalcante |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Engenharia Mecânica, Programa de Pós-Graduação em Engenharia Mecânica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 159 p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0036 seconds