Experimentation exploring the movement of voids within carbon fiber reinforced plastics was performed using fluorescent dye infused into the laminates observed through a transparent mold under ultraviolet light. In situ photography was used as an inspection method for void content during Resin Transfer Molding for these laminates. This in situ inspection method for determining the void content of composite laminates was compared to more common ex-situ quality inspection methods i.e. ultrasonic inspection and cross-section microscopy. Results for localized and total void count in each of these methods were directly compared to test samples and linear correlations between the three test methods were sought. Test coupons were then cut from these laminates and were used to calculate the interlaminar shear strength at certain locations throughout the laminates. Although this research did not adequately observe correlations between results obtained from ultrasonic C-scans, cross-sectional microscopy and in situ photography of the surface, it was seen that the fluid dynamics of the thermosetting epoxy used in this experimentation correlated to results obtained from previous experimentation performed by students at Brigham Young University using vegetable oil as a substitute for resin.
Identifer | oai:union.ndltd.org:BGMYU2/oai:scholarsarchive.byu.edu:etd-8772 |
Date | 01 December 2019 |
Creators | Warner, Wyatt Young |
Publisher | BYU ScholarsArchive |
Source Sets | Brigham Young University |
Detected Language | English |
Type | text |
Format | application/pdf |
Source | Theses and Dissertations |
Rights | http://lib.byu.edu/about/copyright/ |
Page generated in 0.0198 seconds