Carbon nanotubes (CNTs) have great potential in many applications due to their unique structure and properties. However, there are still many unsolved problems hampering their real applications. This thesis focuses on three important issues limiting their applications, namely: (1) direct growth of CNTs without additional catalyst, (2) secondary growth of carbon nanotubes on primary CNT bed without using extra catalyst, (3) and CNT alignment mechanisms during the growth.<p>
The CNTs used in this thesis were prepared by hot filament chemical vapor deposition (CVD) reactor and characterized using scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffractometry (XRD), and Raman spectroscopy. Field electron emission (FEE) properties of the CNTs were also tested.<p>
Oxidation-reduction method was adopted in direct growth of CNTs on Inconel 600 plates and proved effective. The effect of oxidation temperature on the growth of CNTs was studied. It was found that the oxidation temperature had an influence on CNT height uniformity and FEE properties: the higher the treatment temperature, the more uniform the resultant CNTs, and the better the FEE properties of the resultant CNTs. The contribution of different oxides formed at different temperatures were investigated to explain the effect of oxidation temperature on the CNT height uniformity.<p>
Secondary CNTs were grown on primary ones by simply changing the carbon concentration. No additional catalyst was used during the whole deposition process. It was found that synthesizing primary CNTs at extremely low carbon concentration is key factor for the secondary growth without additional catalyst. The CNT sample grown with secondary nanotubes exhibited improved field emission properties.<p>
The effect of bias voltage on growth of vertically aligned carbon nanotubes was investigated. The CNTs grown at -500V shows the best alignment. At the early growth stage, simultaneous growth of randomly oriented and aligned carbon nanotubes was observed. This was consistent with the alignment mechanism involving stress that imposed on catalyst particles on tube tips. Through the observation of CNT growth on the scratched substrates, catalyst particle size was found as another determining factor in the alignment of CNTs. Big catalyst particles promoted aligned growth of CNTs.
| Identifer | oai:union.ndltd.org:USASK/oai:usask.ca:etd-03172009-005447 |
| Date | 24 March 2009 |
| Creators | Yi, Wenwen |
| Contributors | Yang, Qiaoqin, Zhang, Chris, Oguocha, Ikechukwuka, Scott, Robert |
| Publisher | University of Saskatchewan |
| Source Sets | University of Saskatchewan Library |
| Language | English |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://library.usask.ca/theses/available/etd-03172009-005447/ |
| Rights | unrestricted, I hereby certify that, if appropriate, I have obtained and attached hereto a written permission statement from the owner(s) of each third party copyrighted matter to be included in my thesis, dissertation, or project report, allowing distribution as specified below. I certify that the version I submitted is the same as that approved by my advisory committee. I hereby grant to University of Saskatchewan or its agents the non-exclusive license to archive and make accessible, under the conditions specified below, my thesis, dissertation, or project report in whole or in part in all forms of media, now or hereafter known. I retain all other ownership rights to the copyright of the thesis, dissertation or project report. I also retain the right to use in future works (such as articles or books) all or part of this thesis, dissertation, or project report. |
Page generated in 0.0016 seconds