In order to improve the purity of steel castings, the use of special reactive coatings on carbon-bonded ceramic foam filters was explored. Carbon nanotubes were dispersed in water by means of ultrasonic treatment, using xanthan gum to stabilize the nanotubes in suspension and control the rheological behavior. The coatings were applied by cold spraying and binding was achieved during heat treatment in reducing atmosphere, thanks to an artificial pitch added to the slurry. The coated filters were successfully immersed in molten steel for different times. The thickness of the first alumina layer generated at the interface was independent of the immersion time: concentration gradients through its thickness suggested that the formation of this structure is limited by diffusion. Investigation of the steel after solidification by means of ASPEX showed that the presence of the coating influenced the size as well as the chemical composition of the remaining inclusions. Nano-coated filters had the best filtration efficiency (up to 95% for alumina inclusions after 10 s), but longer tests resulted in worse performance. In addition, coatings based on calcium aluminates in combination with carbon showed an efficiency greater than 97% for steel samples taken directly from the melt.
| Identifer | oai:union.ndltd.org:DRESDEN/oai:qucosa:de:qucosa:23218 |
| Date | 23 March 2018 |
| Creators | Storti, Enrico |
| Contributors | Aneziris, Christos G., Colombo, Paolo, Technische Universität Bergakademie Freiberg |
| Source Sets | Hochschulschriftenserver (HSSS) der SLUB Dresden |
| Language | English |
| Detected Language | English |
| Type | doc-type:doctoralThesis, info:eu-repo/semantics/doctoralThesis, doc-type:Text |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0021 seconds