Nitretação e carbonitretação por plasma em aços inoxidáveis e suas influências nas resistências à corrosão e ao desgaste / Plasma nitriding and carbonitriding in stainless steels and their influences in the corrosion and wear resistances

Visando-se determinar as temperaturas mais adequadas de nitretação e carbonitretação por plasma dos aços inoxidáveis austenítico AISI 316L, ferrítico AISI 409 e super duplex ASTM A890 Gr 5A e suas influências nas resistências ao desgaste e à corrosão, amostras desses aços foram tratadas a 400, 450 e 500°C, e submetidas a ensaios micrográficos, de raios X, ensaios microabrasivos e de corrosão. Todas as temperaturas de tratamentos utilizadas nos vários aços estudados produziram camadas com grande regularidade, que tiveram suas espessuras e durezas aumentadas com o aumento da temperatura de tratamento. Em todos os casos, ocorreu um grande aumento nas resistências ao desgaste microabrasivo das amostras nitretadas ou carbonitretadas, em comparação com o substrato, comprovando a efetividade da fase \"S\", produzida nas temperaturas mais baixas, no aumento das durezas e resistências ao desgaste. No caso das amostras tratadas em temperaturas mais elevadas, o nitreto de cromo foi o responsável principal pelo aumento dessa resistência. Verificou-se por meio dos resultados das curvas de polarização anódicas das camadas nitretadas e carbonitretadas a 400°C que, para os três tipos de aços em estudo, tais camadas apresentaram comportamentos semelhantes e superiores aos dos substratos, devido a formação de austenita ou ferrita expandidas. No caso das temperaturas de tratamentos de 450 e 500°C, as amostras carbonitretadas apresentaram desempenho superior ao das nitretadas e, próximos aos dos substratos, não tendo ocorrido degradação dessa propriedade. Os tratamentos de nitretação e carbonitretação por plasma, realizados nas temperaturas adequadas definidas no presente trabalho para os principais tipos de aços inoxidáveis, produziram camadas com elevadas durezas e resistências ao desgaste, sem perdas nas características de corrosão, que inclusive melhoraram em alguns casos, permitem a ampliação do uso dos aços inoxidáveis para situações que requeiram aquelas propriedades. / Aiming to determine the most appropriate temperatures of plasma and carbonitriding of the AISI 316L austenitic stainless steel, AISI 409 stainless steel and ASTM A890 Gr5A super duplex steel and their influence corrosion and wear resistances of those steel samples, they were treated 450 and 500°C, and submitted to micrography analyses, X-ray diffraction, abrasive wear and corrosion tests. All treatment temperatures used in the several studied steels produced layers with great regularity, which increased their thickness and hardness with the increase of the treatment temperature. In all the cases, a great increase occurred in the micro-abrasivive resistance of the nitrided and carbonitrided samples, in comparison with the substrate, proving the effectiveness of the \"S\" phase, produced in the temperatures, in the increase of the hardness and wear resistances. In the the samples treated at higher temperatures, the chromium nitride was the responsible one for the increase in the wear resistance. It was verified through the results of the potenciodinâmicos corrosion the nitrided and carbonitrided layers at 400°C, that for the three types of stee study, such layers presented similar and superior behaviors to that of the substrate, due to austenite or expanded ferrite formation. In the case of the treatment temperatures of 450 and 500°C, the carbonitrided samples presented s performance to the nitrided one and similar performance to the substrates s without the occurrence of any degradation of that property. The plasma nitriding and plasma carbonitriding treatments, carried out in the temperatures defined in the present work, for the principal types of stainless to produce layers with high hardness and wear resistances, without losses corrosion characteristics, which even got better in some cases, allow to expand the use of the stainless steels in situations where those properties are required.

Identiferoai:union.ndltd.org:usp.br/oai:teses.usp.br:tde-15042011-143858
Date14 January 2005
CreatorsOliveira, Antonio Maia de
ContributorsCasteletti, Luiz Carlos
PublisherBiblioteca Digitais de Teses e Dissertações da USP
Source SetsUniversidade de São Paulo
LanguagePortuguese
Detected LanguagePortuguese
TypeTese de Doutorado
Formatapplication/pdf
RightsLiberar o conteúdo para acesso público.

Page generated in 0.0022 seconds