Extended Mercerization Prior to Carboxymethyl Cellulose Preparation

Carboxymethyl cellulose (CMC) is produced commercially in a two-stage process consisting of a mercerization stage, where the pulp is treated with alkali in a water alcohol solution, followed by an etherification stage in which monochloroacetic acid is added to the pulp slurry. In this thesis an extended mercerization stage of a spruce ether pulp was investigated where the parameters studied were the ratio of cellulose I and II, concentration of alkali, temperature and retention time. The influence of the mercerization stage conditions on the etherification stage, were evaluated as the degree of substitution (DS) of the resulting CMC and the filterability of CMC dissolved in water at a concentration of 1%. The DS results suggested that the NaOH concentration in the mercerization stage was the most important of the parameters studied. When the NaOH concentration in the mercerization step was low (9%), a high cellulose II content in the pulp used was found to have no negative impact on the DS of the resulting CMC compared with pulps with only cellulose I. However, when the NaOH concentration was high (27.5%), pulps with high content of cellulose II showed a lower reactivity than those with only cellulose I with respect to the DS of the CMC obtained after a given charge of NaMCA. The results obtained from the filtration ability study of CMC water solutions suggested that both the amount of cellulose II in the original pulp and the temperature had a negative influence on the filtration ability whereas the NaOH concentration in the mercerization stage had a positive influence. The filtration ability was assumed to be influenced highly by the presence of poorly reacted cellulose segments. A retention time between 1-48 h in the mercerization stage had no effect on either the DS or the filtration ability of the CMC. Using NIR FT Raman spectroscopy molecular structures of CMC and its gel fraction were analyzed with respect to the conditions used in the extended mercerization stage. Here it was found that the alkaline concentration had a very strong influence on the following etherification reaction. FT Raman spectra of CMC samples and their gel fractions prepared with low NaOH concentrations (9%) in the mercerization stage indicated an incomplete transformation of cellulose to Na-cellulose before carboxymethylation to CMC. Low average DS values of the CMC, i.e. between 0.42 and 0.50, were yielded. Such CMC dissolved in water caused very thick and semi solid gum-like gels, probably due to an uneven distribution of substituting groups along the cellulose backbone. FT Raman spectra of CMC mercerized with alkaline concentrations at 18.25 and 27.5% in the mercerization stage indicated, however, that all of the cellulose molecules were totally transferred to CMC of high DS, i.e. between 0.88 and 1.05. When dissolved in water such CMC caused gels when they were prepared from ether pulp with a high fraction of cellulose II.

Identiferoai:union.ndltd.org:UPSALLA1/oai:DiVA.org:kau-5947
Date January 2010
CreatorsAlmlöf, Heléne
PublisherKarlstads universitet, Avdelningen för kemiteknik, Karlstad : Karlstad University
Source SetsDiVA Archive at Upsalla University
LanguageEnglish
Detected LanguageEnglish
TypeLicentiate thesis, comprehensive summary, info:eu-repo/semantics/masterThesis, text
Formatapplication/pdf
Rightsinfo:eu-repo/semantics/openAccess
RelationKarlstad University Studies, 1403-8099 ; 2010:22

Page generated in 0.0029 seconds