Výroba a vady ocelových odlitků / Manufacturing and defects of steel castings

A content of this thesis is an analysis of a steel castings production mismatch in Tatra Metallurgy foundry. Most common defects found on castings are gas holes. Thesis shows a theoretical research on casting defects caused by gases in steel castings. It also describes melting and degassing problematics of molten steel and procedures to reduce gas contents. The last part of theoretical research describes oxidation of steel in contact with silica mold. Practical part of thesis analysis production of steel castings to determine the cause of origin of gas holes. Main attention is paid to mold mixture, chemical composition, casting temperatures and casting time. The last chapter metallographically analysis two defected castings to determine the origin of defects. Main attention is paid to shape and chemical composition of gas holes and to morphology of steel inclusions.

Identiferoai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:382108
Date January 2018
CreatorsSmilovský, David
ContributorsČamek, Libor, Záděra, Antonín
PublisherVysoké učení technické v Brně. Fakulta strojního inženýrství
Source SetsCzech ETDs
LanguageCzech
Detected LanguageEnglish
Typeinfo:eu-repo/semantics/masterThesis
Rightsinfo:eu-repo/semantics/restrictedAccess

Page generated in 0.0058 seconds