The thesis deals with the fatigue resistance of material MAR-M 247 at temperatures of 650 °C, 800 °C and 900 °C. Based on the results obtained, curves of durability ("S/N curves") were drawn and the effect of temperature on the fatigue behaviour of nickel-based superalloys MAR-M 247 and IN713 LC was evaluated. Fractographic analysis was used to examine the failure mechanism and the effect of casting defects on the fatigue crack initiation.