Previous issue date: 2009-08-11 / Universidade Federal de Sao Carlos / Alumina supported cobalt catalysts were prepared, characterized and applied in ethanol steam reforming for hydrogen production. The support and the supported catalysts were prepared, respectively, by the solvothermal and precipitation, impregnation and deposition-precipitation methods. Contents of 8 and 15% wt of cobalt were used in the preparation of the catalysts. The cobalt was added by impregnation and deposition-precipitation in the Al2O3 supports using a Co(NO3)2.6H2O solution. The solids were characterized by X-Ray Dispersive Spectroscopy (EDX), Temperature-Programmed Reduction with H2 (TPR-H2), X-Ray Diffraction (XRD), BET Nitrogen Adsorption and Temperature Programmed Oxidation (TPO). The results indicated that the preparation method and the treatment conditions of samples were appropriate for obtaining the wanted compounds. Co3O4 phase was verified for all catalysts through analyses of XRD and TPR-H2 results. Catalytic tests were performed by varying the temperature from 450 to 600°C, with water:ethanol molar ratio of 3:1. The ethanol conversion was superior of 99%, with greater hydrogen yield at 600°C. The lower carbon deposition was observed in catalysts prepared with solvothermal/impregnation methods at 450°C. / Neste trabalho foram preparados e caracterizados catalisadores de cobalto suportados em alumina, com o objetivo de avalia-los no processo de reforma a vapor do etanol para producao de hidrogenio. Os suportes e os catalisadores suportados foram preparados, respectivamente, pelos metodos solvotermico e precipitacao, impregnacao e deposicao-precipitacao. Na preparacao dos catalisadores utilizou-se teor de 8% e 15% em massa de cobalto, que foi adicionado por impregnacao e deposicao- precipitacao, usando solucao aquosa de Co(NO3)2.6H2O. Para caracterizacao dos solidos, as tecnicas utilizadas foram Espectroscopia Dispersiva de Raios-X (EDX), Reducao a Temperatura Programada com H2 (RTP-H2), Difracao de Raios-X pelo metodo do po (DRX), Adsorcao de Nitrogenio pelo metodo B.E.T e Oxidacao a Temperatura Programada (TPO). Os resultados indicaram que o metodo de preparacao e as condicoes de tratamento das amostras foram adequados para obtencao dos compostos desejados. Atraves dos resultados de DRX e RTP-H2 verificou-se a formacao da fase Co3O4 em todos os catalisadores. Os testes cataliticos foram realizados variando-se a temperatura de 450 a 600°C e razao molar agua:etanol na alimentacao igual a 3:1. A conversao do etanol foi sempre superior a 99%, com maior rendimento a hidrogenio a 600°C. Observou-se baixa deposicao de carbono nos catalisadores preparados pelos metodos solvotermico/impregnacao a 450°C.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufscar.br:ufscar/4028 |
Date | 11 August 2009 |
Creators | Garcia, Silmara Rodrigues |
Contributors | Assaf, José Mansur |
Publisher | Universidade Federal de São Carlos, Programa de Pós-graduação em Engenharia Química, UFSCar, BR |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | application/pdf |
Source | reponame:Repositório Institucional da UFSCAR, instname:Universidade Federal de São Carlos, instacron:UFSCAR |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.002 seconds