The Master thesis deals with utilization possibilities of fly ash after selective non-catalytic reduction (SNCR) process for Portland cement preparation as a correction component to the raw material with regard to contaminated fly ash by ammonium sulphate or ammonium hydrogensulfate that is one of the products from SNCR process. Presented thesis was focused on behaviour of raw meal with ammonia hydrogensulfate contaminated fly ash after SNCR during burning of Portland clinker in simulated kiln conditions. The thesis deals with Portland clinker preparation from this kind of raw mix and it studies mainly clinker quality, clinker phases and structure. Quantitative phase composition of prepared samples of clinker was performed by optical microscopy measurements using point counting method and XRD analysis (Rietveld method). Hydration heat flow of prepared clinker was measured by Isothermal Calorimetry. TG-DTA analysis of prepared raw meal was studied due to better comparison of prepared samples and better understanding of processes during burning process.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:240583 |
Date | January 2016 |
Creators | Kozlová, Romana |
Contributors | Šoukal, František, Opravil, Tomáš |
Publisher | Vysoké učení technické v Brně. Fakulta chemická |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.003 seconds