In this dissertation the effects of different types of Pulverized Fuel Ash (PF A)-types on the workability of cementitious pastes containing relative large amounts of PF A were investigated. The different types of PF A were produced at the same source thus they were chemically similar but differed in terms of average particle size and size distribution (grading). By using a two-point measurement technique based on flow through a J-shaped tube it was possible to detect relative small differences in workability between pastes. It was found and concluded that the different types of PFA had a significant effect on the workability of pastes containing cement and PFA as well as PF A alone. The physical differences between the PF A-types were quantified and their effects on workability investigated. It was concluded that PF A with a broader particle size distribution range produced pastes with higher workability at constant water content. It was found that compressive strength as measured after 28 days were solely a function of the water/cementitious ratio for the curing regime employed. It was concluded that for curing conditions used the type of PF A used could have a significant effect on compressive strength when constant workability is required. / Dissertation (MSc (Transportation))--University of Pretoria, 2006. / Civil Engineering / unrestricted
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:up/oai:repository.up.ac.za:2263/26113 |
| Date | 08 July 2005 |
| Creators | Pretorius, Jan Hendrik Christoffel |
| Contributors | Kearsley, Elsabe P., upetd@up.ac.za |
| Publisher | University of Pretoria |
| Source Sets | South African National ETD Portal |
| Detected Language | English |
| Type | Dissertation |
| Rights | © 2002, University of Pretoria. All rights reserved. The copyright in this work vests in the University of Pretoria. No part of this work may be reproduced or transmitted in any form or by any means, without the prior written permission of the University of Pretoria. |
Page generated in 0.002 seconds