Perlite is a glassy volcanic rock that contains approximately 70-75% silica and 12-18% alumina.
There are very large perlite reserves in the world (~6700 million tons) and approximately two thirds of these is in Turkey.
Due to its high amounts of silica and alumina, at the beginning of such a study, it seemed that it would be worth first to find out whether perlite possesses sufficient pozzolanic property when it is a finely divided form and then to investigate whether it could be used as a pozzolanic addition in producing blended cements.
In this study, perlites from two different regions (izmir and Erzincan) were tested for their pozzolanic properties. After obtaining satisfactory results, grindability properties of the clinker, perlites and their different combinations were investigated. Several blended cements with different fineness values and different perlite amounts were produced by either intergrinding or separate grinding methods. The tests performed on the cement pastes and mortars containing the blended cements produced were as follows: Water requirement, normal consistency, setting time, soundness, compressive strength, rapid chloride permeability, resistance to sulfate attack and resistance to alkali-silica reactions.
The results showed that Turkish perlites possess sufficient pozzolanic characteristics to be used in cement and concrete industry. Moreover, the properties tested in this study satisfied the requirements stated in the standards for blended cements. The durability of the mortars was found to be improved by 20% or more perlite incorporation.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/3/12605964/index.pdf |
| Date | 01 March 2005 |
| Creators | Erdem, Tahir Kemal |
| Contributors | Erdogan, Turhan Y |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | Ph.D. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for public access |
Page generated in 0.0019 seconds