Tese (doutorado) - Universidade Federal de Santa Catarina, Centro Tecnológico, Programa de Pós-Graduação em Ciência e Engenharia de Materiais, Florianópolis, 2015. / Made available in DSpace on 2015-10-27T03:06:02Z (GMT). No. of bitstreams: 1
335762.pdf: 3903030 bytes, checksum: e2d9016ce81effa053940d9143555e48 (MD5)
Previous issue date: 2015 / Nanoaluminato de magnésio (MgAl2O4) foi sintetizado com sucesso por reação de combustão em solução, utilizando como combustíveis glicerinas loira e bruta, provenientes do biodiesel. O aluminato de magnésio obtido, em pó, foi preparado utilizando?se duas rotas de processamento denominadas de aquecimento convencional e aquecimento rápido. As etapas iniciais foram as mesmas, isto é, os precursores, Al(NO3)3.9H2O e Mg(NO3)2.6H2O, em proporção molar de 2:1, foram dissolvidos em 20% (em massa) de água deionizada e submetidos a agitação magnética, com aquecimento a 70 °C até o início da reação, com a adição dos combustíveis. No aquecimento convencional foram utilizados como combustíveis sacarose, glicerina pura, glicerina loira, glicerina loira seca por 24h, glicerina loira seca por 24h +gel, gel e glicerina bruta. No aquecimento rápido, os combustíveis utilizados foram glicerina loira e bruta. As espumas cerâmicas foram produzidas por dois métodos, isto é, a termoespumação e a réplica polimérica, utilizando a mesma suspensão base. Os pós e as espumas produzidas foram caracterizados do ponto de vista de suas propriedades macro e microestruturais e de suas propriedades mecânicas e térmicas. Os resultados mostraram que somente o pó produzido por aquecimento rápido, utilizando glicerina loira como combustível, apresentou fase única formada de MgAl2O4. Este pó apresentou tamanhos (diâmetros) de partículas primárias ou cristalitos de 9 nm e área superficial de 112 m2.g-1. As espumas de MgAl2O4 produzidas por réplica e termoespumação (queimadas a 1600 °C/120 min, usando pó calcinado a 900 °C/120 min) apresentaram porosidades de 94% e 97% e resistência mecânica de 1,0 e 0,10 MPa, respectivamente. Estas espumas, aplicadas como queimadores porosos, operaram em condições semelhantes à queimadores porosos de Al2O3 para um único ciclo térmico.<br> / Abstract : Nanosized magnesium aluminate (MgAl2O4) was successfully synthesized by combustion reaction in solution using as fuels crude and blonde glycerin from the biodiesel. The magnesium aluminate powder obtained was prepared using two processing routes called conventional heating and fast heating. The initial steps are the same, i.e., precursors, Al(NO3)3.9H2Oand Mg(NO3)2.6H2O in molar ratio of 2:1 were dissolved in 20% (by weight) of deionized water and subjected to magnetic stirring with heating at 70°C until the reaction has started with the addition of fuels. In conventional heating saccharose, pure glycerin, blonde glycerin, blonde glycerin dried for 24 hours, blonde glycerin dried for 24 hours + glycerin gel, gel and crude glycerin were used as fuels. In the fast heating, the blonde and crude glycerins were used as fuels. Ceramic foams were produced by two methods, i.e., thermal foaming and by the replication method using the same base suspension. The powders and the ceramic foams produced were characterized from the point of view of their macro and microstructural properties and their mechanical and thermal properties. The results showed that only the powder produced by fast heating using blonde glycerin as fuel, showed the MgAl2O4 single phase. This powder had sizes (diameters) of primary particles or crystallites of 9 nm and surface area of 112 m2.g-1. The MgAl2O4 foams produced by the thermal foaming and the replication method (fired at 1600°C/120 min using powders calcined at 900°C/120min) had porosity of 94% and 97% and mechanical strength of 1.0 to 0.10Mpa, respectively. These ceramic foams, applied as porous burners, operated under conditions similar to porousAl2O3burnersfor a single thermal cycle.
Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufsc.br:123456789/135777 |
Date | January 2015 |
Creators | Moraes, Graziela Guzi de |
Contributors | Universidade Federal de Santa Catarina, Oliveira, Antonio Pedro Novaes de |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
Format | 161 p.| il., grafs., tabs. |
Source | reponame:Repositório Institucional da UFSC, instname:Universidade Federal de Santa Catarina, instacron:UFSC |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.2427 seconds