Orientador: Lourenço Correr Sobrinho / Tese (doutorado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-06T14:17:07Z (GMT). No. of bitstreams: 1
Tango_RubensNisie_D.pdf: 517454 bytes, checksum: 78bb278313f8acd3dca9e0eb5588eb01 (MD5)
Previous issue date: 2006 / Resumo: Este estudo avaliou através do teste de dureza Knoop (KHN), a profundidade de polimerização do cimento resinoso Enforce, dual e fotoativado, quando fotoativados através da cerâmica (HeraCeram) ou do compósito (Artglass), com diferentes aparelhos fotoativadores. A fotoativação foi realizada com os aparelhos de luz de lâmpada halógena (XL2500) - QTH, luz emitida por diodos (Ultrablue 1s) - LED, ambos por 40 segundos, e aparelho de arco de plasma de xenônio (Apollo 95E) por 3 segundos - P AC. As faces vestibulares de incisivos bovinos foram planificadas e hibridizadas com o sistema adesivo Prime & Bond 2.1. Sobre estas superficies foi assentada uma matriz de borracha preta e opaca (lmm de espessura / 5mm de diâmetro), a qual foi preenchida com o cimento. Um disco de material para faceta (l,5mm de espessura) foi comprimido digitalmente sobre este conjunto para padronização da espessura de cimento e extravasamento dos excessos. A fotoativação foi realizada, com a ponta ativa dos aparelhos em contato com os illlteriais para faceta, sendo que nos grupos controle, a ativação foi realizada diretamente. Após armazenamento em ambiente seco e escuro (24h/37°C), as amostras (n=IO) foram seccionadas para mensuração dos valores de dureza (KHN), obtidos em aparelho microdurômetro (50gf de carga/ 15s). Os dados dos cimentos, dual e fotoativado, foram analisados separadamente. Para ambos, os dados foram submetidos à análise de variância de 3 fatores. Posteriormente, para o cimento dual foi aplicado o teste de Tukey e para o cimento fotoativado, o teste de Duncan (a=0,O5). Para ambos os cimentos, foram verificados que os valores de dureza diminuem com o aumento da profundidade de polimerização. Além disso, para ativação direta e através de HeraCeram, os maiores valores de dureza foram obtidos com LED, seguido por QTH e P AC. Para Artglass, no modo dual, valores de dureza similares foram obtidos com os 3 aparelhos fotoativadores. Já no modo foto ativado, os maiores valores foram obtidos com QTH, seguido pelo LED e P AC, respectivarrente. O aparelho P AC, com tempo de exposição de 3 segundos, mostrou-se ineficaz na polimerização do cimento no modo fotoativado através dos materiais para faceta. O efeito dos materiais para faceta foi distinto para cada aparelho foto ativador / Abstract: This study evaluated the polymerization depth of the dual-cure and light-cure resin cement Enforce, light-cured through ceramic (HeraCeram), or composite (Artglass), with different light curing units, by Knoop hardness (KHN) test. Light curing was carried out using conventional quartz tungsten halogen light (XL2500) - QTH, light emitting diodes (Ultrablue ls) - LED, both for 40s and, xemn plasma are (Apollo 95E) for 3s P AC. Bovine incisors had their buccal faces flattened and hybridized with the bond agent rime & Bond 2.1. On these surfaces, a black opaque mold (lmm thickness/ 5mm in diameter) was seated and filled with cement. A disc of the veneering material (l.5mm thickness) was compressed digitally over this set for cement thickness standardization and excesses remova!. Light curing was carried out with the light curing unit tip in contact with the veneering materiaIs. ln the control groups, resin cement was light cured directly. After dry storage at dark (24h/37°C), samples (n=lO) were sectioned for hardness (KHN) measurements, taken in a microhardness tester (50gf load/ 15s). Data of resin cement hardness, for dual cure and light cure, were analyzed separately. For both, data were submitted to three-way ANOV A. After that, Tukey's test was applied for dual cure resin cement, and for light cure cement Duncan's test was used (cx=.05). For both cements, it was verified that hardness decreased with the increase in polymerization depth. Besides that, for direct light curing and for light curing through HeraCeram, the highest hardness values were obtained with LED, followed by QTH and P AC. ln the dual cure resin cement beneath Artglass, similar hardness values were verified with the 3 light curing units. However, in light cure resin cement, the highest means were observed with QTH, followed by LED and PAC, respectively. PAC showed to be inefficient to polymerize the light cure resin cement beneath veneering materiaIs with 3s exposure time. The light transmission attenuating effect of veneering materiaIs was distinct for each light-curing unit / Doutorado / Materiais Dentarios / Mestre em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289586 |
| Date | 04 March 2006 |
| Creators | Tango, Rubens Nisie |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Correr Sobrinho, Lourenço, 1960-, Konno, Alysson Noriyuki Kajishima, Consani, Rafael Leonardo Xediek, Consani, Simonides, Junior, Tarcisio Jose de Arruda Paes |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | 68p. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0033 seconds