Made available in DSpace on 2015-01-26T13:21:23Z (GMT). No. of bitstreams: 0
Previous issue date: 2014-03-07Bitstream added on 2015-01-26T13:30:35Z : No. of bitstreams: 1
000801060.pdf: 1865176 bytes, checksum: 4bf3c078c38466a29f080b8396113a82 (MD5) / Apesar das restaurações em cerâmicas Y-TZP (Yttria tetragonal zirconia polycrystal) estarem sendo cada vez mais utilizadas na prática clínica devido às suas excelentes propriedades, tratamentos de superfície ainda são necessários para a melhoria de sua adesão com cimentos resinosos. Este estudo avaliou a influência da partícula e do momento do jateamento na caracterização superficial de uma cerâmica Y-TZP e na sua resistência de união com cimento resinoso. Espécimes de zircônia foram submetidos aos seguintes tratamentos com jateamento: partículas de Al2O3 de 50 μm; partículas de Al2O3 de 120 μm; partículas de Al2O3 de 30 μm modificadas por sílica (Rocatec Soft); e partículas de Al2O3 de 110 μm modificadas por sílica (Rocatec Plus). O jateamento foi realizado em três momentos diferentes: após a sinterização da zircônia (PÓS) (grupo controle); antes da sinterização da zircônia (PRÉ); e antes/após a sinterização (PP). A caracterização da superfície da zircônia incluindo rugosidade superficial (n=10), molhamento (n=10), microscopia eletrônica de varredura (n=2) e composição elementar (n=2) foi realizada. O teste de resistência de união ao cisalhamento (RC) (n=11) foi conduzido após a termociclagem dos espécimes (10000 ciclos – 5°C e 55°C). O modo de fratura foi analisado através de um estereomicroscópio (x 20). Rugosidade, molhamento e RC foram analisados através da ANOVA dois fatores e o teste de Tukey (α=,05). Nos grupos PRÉ e PP, a rugosidade aumentou de acordo com o tamanho da partícula. Independentemente da partícula, o grupo PÓS apresentou os menores valores de rugosidade, enquanto os grupos PRÉ e PP não apresentaram diferença significativa entre eles. De uma maneira geral, as partículas de Al2O3 de 120 μm e Rocatec Plus apresentaram os maiores e menores ângulos de contato. Com relação à partícula, os grupos PRÉ e PP exibiram o maior e o menor ângulo de contato... / Despite Y-TZP (yttria tetragonal zirconia polycrystal) ceramic restorations became widely used in clinical practice due to its excellent properties, surface treatments are required for the improvement of the adhesion with resin cements. This study evaluated the influence of the particle and air abrasion moment on the surface characterization of a Y-TZP ceramic and its bond strength with a resin cement. Zirconia specimens were air-abraded with the following particles: 50 μm Al2O3 particles; 120 μm Al2O3 particles; 30 μm silica-coated Al2O3 particles (Rocatec Soft); and 110 μm silica-coated Al2O3 particles (Rocatec Plus). Air-abrasion was performed in 3 different moments: after zirconia sintering (AS)(control group); before zirconia sintering (BS); before and after zirconia sintering (BAS). The zirconia surface characterization including roughness (n=10), wettability (n=10), morphology (n=2) and elemental composition (n=2) was performed. The SBS test (n=11) was conducted after thermal cycling (10,000 cycles - 5ºC and 55ºC). Failure mode was determined with a stereomicroscope (×20). Roughness, wettability and SBS data were analyzed by two-way ANOVA and Tukey’s test (α=.05). For BS and BAS, the roughness increased according to the increase in the particle size. AS showed the lowest roughness, while BS and BAS did not exhibit significant difference each other. In general, Rocatec Plus and 120 μm Al2O3 particles provided the lowest and the highest contact angle. BS and BAS exhibited the highest and the lowest contact angle. The particle as well as the air-abrasion moment did not promote regular morphological patterns. The additional presence of the Si element in the groups abraded with silica-modified Al2O3 particles was the only difference observed between these groups and those abraded with Al2O3 particles. For BS, the highest and the lowest SBS was provided by 120 μm Al2O3 particles and Rocatec Soft. For BAS and AS, the highest SBS...
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/113928 |
| Date | 07 March 2014 |
| Creators | Martins, Samira Branco [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Fonseca, Renata Garcia [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 97 f. : il. color. - |
| Source | Aleph, reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1 |