Previous issue date: 2018-02 / CNPq / As misturas mornas surgem como uma opção para a redução das temperaturas de usinagem e compactação, uma alternativa que proporciona vantagens econômicas, ambientais e técnicas. Este trabalho trata da utilização das ceras de carnaúba do tipo 1, nos teores de 1, 2 e 3% (m/m), como aditivo incorporado as misturas asfálticas para a obtenção de misturas mornas. A cera do tipo 1 foi utilizada para modificar o ligante 50/70 e foram avaliados seus efeitos a partir de ensaios empíricos: penetração, ponto de amolecimento e ensaios no viscosímetro rotacional. O ligante asfáltico modificado com 2 e 3% de cera de carnaúba apresentou uma considerável diminuição das temperaturas de usinagem (TU) de 9°C, reduzindo as emissões de gases poluentes (CO2 e VOCs, por exemplo) e o gasto energético. Foi utilizado o método SUPERPAVE, com objetivo de produzir os corpos de prova que foram utilizados para fazer a análise mecânica. Com o propósito de avaliar os efeitos da redução das temperaturas de produção e compactação e a influência da incorporação do aditivo na mistura asfáltica, foram realizados ensaios mecânicos: Resistência à Tração, Modulo de Resiliência, Dano por Umidade (Lottman), Fadiga, Flow Number, Cântabro e Módulo Dinâmico. A mistura com 2% de cera de carnaúba apresentou melhores resultados em relação as análises mecânica e reológica, uma maior redução das temperatura de usinagem e compactação. Espera-se que tal pesquisa possa contribuir para a redução dos danos causados ao meio ambiente, maior viabilidade técnica e econômica. Portanto, a cera de carnaúba cumpre algumas exigências mecânicas e reológicas para a sua utilização como aditivo em misturas asfálticas mornas. / Warm mixtures appear as an option for reducing temperature machining and compression, an alternative that provides economic advantages, environmental and technical. This paper deals with the use of carnauba wax type 1, the levels 1, 2 and 3% (m / m), as an additive incorporated into the asphalt mixtures for obtaining mixtures of lukewarm. Wax type 1 was used to modify the binder 50/70 and evaluated its effects from empirical tests: penetration point testing the softening and rotational viscometer. The modified asphalt binder 2:03% carnauba wax showed a considerable reduction in temperature machining (TU) of 9 ° C, reducing pollutant emissions (CO 2 and VOCs, for example) and energy expenditure. SUPERPAVE the method was used, in order to producing the specimens which were used to make mechanical analysis. As order to evaluate the effects of reducing the production and compaction temperatures and the influence of the incorporation of the additive in the asphalt mixture, tests were conducted Mechanical: tensile strength, modulus of resilience, moisture damage (Lottman) Fatigue, Flow Number, Cántabro and dynamic modulus. The mixture with 2% wax carnauba showed better results than the mechanical and rheological analysis, further reducing the temperature machining and compression. It is expected that such research can contribute to the reduction of damage to the environment, most technical and economic feasibility. Therefore, carnauba wax meets certain requirements mechanical and rheological properties for use as an additive in warm asphalt mixes.
Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/402 |
Date | 17 April 2018 |
Creators | MORAES, Thalita Maria Ramos Pôrto de. |
Contributors | LUCENA, Adriano Elísio de Figueiredo Lopes., ALBUQUERQUE, Fernando Silva., RODRIGUES, John Kennedy Guedes. |
Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM ENGENHARIA CIVIL E AMBIENTAL, UFCG, Brasil, Centro de Tecnologia e Recursos Naturais - CTRN |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | Portuguese |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0015 seconds