The positive temperature coefficient of resistivity (PTCR) sensors is resistor materials that undergo a sharp change in resistivity at a designed Curie temperature due to its unique structure and chemical composition. This effect serves important control functions in a wide variety of electronic circuitry and similar applications. Conventional calcining of mixed oxides method (CMO) is used for fabricating lanthanum doped barium titanate (BaTiO3) for PTCR behaviour through solid-state-sintering route, at 1100°C, 1350°C. Two batches of samples were fabricated at low and high sintering temperatures of 1100°C, 1350°C respectively. The effect of different concentrations of donor dopant on BaTiO3 on the electrical properties of Ba(1-x)LaxTiO3 with x= 0.0005, 0.001, 0.002, 0.0025, 0.003 mol%, is investigated at low sintering temperature. The influence of lantanum doping with Al2O3+SiO2+TiO2 (AST) as sintering aids on the electrical properties of Ba(1-x)LaxTiO3 with x= 0.0005, 0.001, 0.003 mol%, is also investigated. The results of the electrical characterization for the first batch of samples showed an increase in room temperature resistance with increaisng donor concentration. Also the results of the electrical characterization for the second batch of samples also showed the same increase in room temperature resistance with increasing donor concentration. For first batch of sensors the high room temperature resistance keeps the jump small and these materials showed V-shaped NTCR-PTCR multifunctional cryogenic sensor behavior with a strong negative coefficient of resistance effect at room temperature.Where as the second batch of sensors showed few orders of magnitude rise in resistivity values. The La-doped BaTiO3 ceramics co-doped with Mn gives an enhanced PTCR effect which can be exploited for various sensor applications.
| Identifer | oai:union.ndltd.org:ADTP/281672 |
| Creators | Puli, Venkata Sreenivas |
| Publisher | AUT University |
| Source Sets | Australiasian Digital Theses Program |
| Detected Language | English |
| Rights | All items in ScholarlyCommons@AUT are provided for private study and research purposes and are protected by copyright with all rights reserved unless otherwise indicated. |
Page generated in 0.0016 seconds