Previous issue date: 2010-03-31 / The chemical recycling of polyolefins has been the focus of increasing attention owing
potential application as a fuel and as source chemicals. The use of plastic waste contributes to
the solution of pollution problems.The use of catalysts can enhance the thermal degradation of
synthetic polymers, which may be avaliated by Themogravimetry (TG) and mass
spectrometry (MS) combined techniques. This work aims to propose alternatives to the
chemistry recycling of low-density polyethylene (LDPE) on mesoporous silica type SBA-15
and AlSBA-15.The mesoporous materials type SBA-15 and AlSBA-15 were synthesized
through the hydrothermal method starting from TEOS, pseudobohemite, cloridric acid HCl
and water. As structure template was used Pluronic P123. The syntheses were accomplished
during the period of three days. The best calcination conditions for removal of the organic
template (P123) were optimized by thermal analysis (TG/DTG) and through analyses of Xray
diffraction (XRD), infrared spectroscopy (FT-IR), nitrogen adsorption and scanning electron
microscopy (SEM) was verified that as much the hydrothermal synthesis method as the
calcination by TG were promising for the production of mesoporous materials with high
degree of hexagonal ordination. The general analysis of the method of Analog Scan was
performed at 10oC/min to 500 oC to avoid deterioration of capillary with very high
temperatures. Thus, with the results, we observed signs mass/charge more evident and, using
the MID method, was obtained curve of evolution of these signals. The addition of catalysis
produced a decrease in temperature of polymer degradation proportional to the acidity of the
catalyst. The results showed that the mesoporous materials contributed to the formation of
compounds of lower molecular weight and higher value in the process of catalytic degradation
of LDPE, representing an alternative to chemical recycling of solid waste / A reciclagem qu?mica de poliolefinas tem sido foco de crescente aten??o, devido ao
seu uso potencial como combust?vel e como fonte de produtos qu?micos. O aproveitamento de
res?duos pl?sticos contribui para a solu??o dos problemas de polui??o. O uso de catalisadores
adequados pode facilitar a degrada??o t?rmica de pol?meros sint?ticos, que pode ser avaliada
por termogravimetria e espectrometria de massas. Este trabalho teve como objetivo avaliar
uma alternativa de reciclagem qu?mica de polietileno de baixa densidade (PEBD) sobre s?lica
mesoporosa tipo SBA-15 e AlSBA-15 utilizando termogravimetria e espectrometria de
massas.Os materiais mesoporosos tipo SBA-15 e AlSBA- 15 foram sintetizados atrav?s do
m?todo hidrot?rmico partindo de tetraetilortosilicato TEOS, pseudobohemita, ?cido
clor?drico - HCl e ?gua destilada. Como direcionador estrutural foi utilizado Pluronic P123
(copol?mero tribloco). As s?nteses foram realizadas durante um per?odo de tr?s dias. As
melhores condi??es de calcina??o para remo??o do direcionador org?nico (P123) foram
otimizadas por an?lise t?rmica (TG/DTG) e atrav?s de an?lises por difra??o de raios X
(DRX), espectroscopia na regi?o do infravermelho (FTIR), adsor??o de nitrog?nio e
microscopia eletr?nica de varredura (MEV) se verificou que tanto o m?todo de s?ntese
hidrot?rmico, como tamb?m as condi??es de calcina??o baseadas nos estudos cin?ticos por
termogravimetria (TG) foram promissores ? produ??o de materiais mesoporosos com alto
grau de ordena??o hexagonal. Os estudos de decomposi??o e evolu??o de gases foram
realizados em uma termobalan?a acoplada a um espectr?metro de massas. A an?lise geral das
amostras com o m?todo de Scan Analog foi realizada a 10?C/min at? 500?C para n?o
deteriorar o capilar com temperaturas muito altas. Assim, com os resultados foi poss?vel
observar os sinais massa-carga mais evidentes e, empregando o m?todo MID, foi obtida a
curva de evolu??o desses sinais. A adi??o de catalisadores produziu uma diminui??o na
temperatura de degrada??o do pol?mero proporcional ? acidez do catalisador. Os resultados
obtidos, mostraram que os materiais mesoporosos contribu?ram para a forma??o de compostos
de menor massa molecular e maior valor agregado no processo de degra??o catal?tica do
PEBD, representando uma alternativa de reciclagem qu?mica destes res?duos s?lidos
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.ufrn.br:123456789/17787 |
| Date | 31 March 2010 |
| Creators | Fernandes, Glauber Jos? Turolla |
| Contributors | CPF:35530502415, http://lattes.cnpq.br/9770622597949866, Delgado, Regina Celia de Oliveira Brasil, CPF:87774151400, http://lattes.cnpq.br/1862313412291911, Qunitella, Solange Assun??o, CPF:32128088372, http://lattes.cnpq.br/7521511093074177, Castro, Francisco Laerte de, CPF:77862589491, http://lattes.cnpq.br/2913544384537886, Ara?jo, Ant?nio Souza de |
| Publisher | Universidade Federal do Rio Grande do Norte, Programa de P?s-Gradua??o em Qu?mica, UFRN, BR, F?sico-Qu?mica; Qu?mica |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | application/pdf |
| Source | reponame:Repositório Institucional da UFRN, instname:Universidade Federal do Rio Grande do Norte, instacron:UFRN |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds