ABSTRACT
PRODUCTION OF CARBON NANOTUBES BY
CHEMICAL VAPOR DEPOSITION
Ayhan, Umut BariS
M.S., Department of Chemical Engineering
Supervisor: Prof. Dr. Gü / ngö / r Gü / ndü / z
Co-Supervisor: Assoc. Prof. Dr. Burhanettin Ç / iç / ek
July 2004, 75 pages
Carbon nanotubes, which is one of the most attractive research subject for scientists, was synthesized by two different methods: Chemical vapor deposition (CVD), a known method for nanotube growth, and electron beam (e-beam), a new method which was used for the first time for the catalytic growth of carbon nanotubes.
In both of the methods, iron catalyst coated silica substrates were used for the carbon nanotube growth, that were prepared by the Sol-Gel technique using aqueous solution of Iron (III) nitrate and tetraethoxysilane. The catalytic substrates were then calcined at 450 ° / C under vacuum and iron was reduced at 500° / C under a flow of nitrogen and hydrogen.
In CVD method the decomposition of acetylene gas was achieved at 600 ° / C and 750 ° / C and the carbon was deposited on the iron catalysts for nanotube growth. However, in e-beam method the decomposition of acetylene was achieved by applying pulsed high voltage on the gas and the carbon deposition on the silica substrate were done.
The samples from both of the methods were characterized using transmission electron microscopy (TEM) and Raman spectroscopy techniques. TEM images and Raman spectra of the samples show that carbon nanotube growth has been achieved in both of the method. In TEM characterization, all nanotubes were found to be multi-walled carbon nanotubes (MWNT) and no single-walled carbon nanotubes (SWNT) were pictured. However, the Raman spectra show that there are also SWNTs in some of the samples.
| Identifer | oai:union.ndltd.org:METU/oai:etd.lib.metu.edu.tr:http://etd.lib.metu.edu.tr/upload/12605199/index.pdf |
| Date | 01 August 2004 |
| Creators | Ayhan, Umut Baris |
| Contributors | Gunduz, Gungor |
| Publisher | METU |
| Source Sets | Middle East Technical Univ. |
| Language | English |
| Detected Language | English |
| Type | M.S. Thesis |
| Format | text/pdf |
| Rights | To liberate the content for public access |
Page generated in 0.0103 seconds