Cr-Mo plieno suvirintų jungčių terminio apdirbimo tyrimas / The research of Cr-Mo steel welded joints post weld heat treatment

In the final thesis there is analyzed of chrome-molybdenum steel (5%Cr-0,5%Mo) welded joints strength properties dependence on thermal treatment after welding procedures investigation material. Welded joints ultimate strength and impact strength were determined, changing heat treatment after welding temperatures and exposure time. Heat treatment temperature and time parameter was used to systemize investigation. Received results showed that when performing heat treatment after Cr-Mo steel (5%Cr-0,5%Mo) welding, increasing temperature and time parameter values, welded joints strength characteristics values go down. Welded joints after heat treatment strength properties dependence on temperature and time parameter were determined, increasing this parameter, ultimate strength and impact strength values go down.

Identiferoai:union.ndltd.org:LABT_ETD/oai:elaba.lt:LT-eLABa-0001:E.02~2005~D_20050622_121206-78578
Date22 June 2005
CreatorsKumšlytis, Vigantas
ContributorsČernašėjus, Olegas, Vilnius Gediminas Technical University
PublisherLithuanian Academic Libraries Network (LABT), Vilnius Gediminas Technical University
Source SetsLithuanian ETD submission system
LanguageLithuanian
Detected LanguageEnglish
TypeMaster thesis
Formatapplication/pdf
Sourcehttp://vddb.library.lt/obj/LT-eLABa-0001:E.02~2005~D_20050622_121206-78578
RightsUnrestricted

Page generated in 0.0016 seconds