Neste trabalho apresenta-se um estudo de caracterizaÃÃo de blocos cerÃmicos estruturais. A finalidade principal à estudar aspectos da microestrutura desses blocos, determinantes no processo de usa ruptura à compressÃo. SÃo utilizados 18 blocos cerÃmicos estruturais, submetidos à compressÃo atà a ruptura. Para a caracterizaÃÃo da microestrutura, retiram-se amostras de blocos especÃficos de acordo com os resultados obtidos nos ensaios de resistÃncia à compressÃo. A observaÃÃo da microestrutura à realizada com a utilizaÃÃo de microscopia Ãtica e de microscopia eletrÃnica de varredura. SÃo tambÃm realizadas anÃlises de composiÃÃo quÃmica atravÃs de EDS âenergy dispersion spectrometryâ. Com a anÃlise dos resultados identifica-se a existÃncia de relaÃÃes fundamentais entre formato e disposiÃÃo dos poros presentes na microestrutura dos blocos e o processo de ruptura à compressÃo. Com base nestas relaÃÃes, propÃe-se um esquema teÃrico para o mecanismo de ruptura dos blocos cerÃmicos estruturais. TambÃm à apresentado um estudo quantitativo da microestrutura (metalografia) dos blocos cerÃmicos estruturais. Adicionalmente sÃo confeccionados prisnas ( dois blocos unidos por uma junta de argamassa) e prismas contrafiados ( formados por um bloco e meio na base e com trÃs fiadas de altura, unidos por juntas verticais e horizontais) com trÃs diferentes traÃos de argamassa. Determina-se para os prismas e para os prismas contrafiados a resistÃncia à compressÃo. SÃo, entÃo, propostas equaÃÃes relacionadas as propriedades medidas para cada um dos elementos ( prismas e prismas contrafiados) estudados. / This paper presents a study of structural characterization of ceramic blocks. The main purpose is to study aspects of the microstructure of these blocks, in the process of determining uses compression rupture. 18 blocks are used structural ceramics subjected to compression up to failure. To characterize the microstructure, withdraw samples of particular blocks in accordance with the results of the tests of resistance to compression. The observation of the microstructure is performed using optical microscopy and scanning electron microscopy. They are also chemical composition analysis using EDS "energy dispersion spectrometry." By analyzing the results identified the existence of relationships between fundamental shape and arrangement of pores present in the microstructure of the blocks and the process of compression rupture. Based on these relationships, it is proposed a conceptual framework for the mechanism of breaking the ceramic block structure. It also presents a quantitative study of the microstructure (metallography) of structural ceramic blocks. Additionally prisnas are made (two blocks joined by a mortar) and contrafiados prisms (formed by a block and a half at the base and with three rows of height, connected by vertical and horizontal joints) with three different traces of mortar. Is determined for the prisms and the prisms contrafiados the compressive strength. Are then proposed equations relating the measured properties for each element (contrafiados prisms and prisms) studied.
Identifer | oai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:5275 |
Date | 20 April 2005 |
Creators | Carlos Eduardo de FranÃa Villar |
Contributors | Hamilton Ferreira Gomes de Abreu, Luis Alberto de Melo Carvalho, MÃrcio Roberto Silva CorrÃa |
Publisher | Universidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em Engenharia e CiÃncia de Materiais, UFC, BR |
Source Sets | IBICT Brazilian ETDs |
Language | Portuguese |
Detected Language | English |
Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
Format | application/pdf |
Source | reponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC |
Rights | info:eu-repo/semantics/openAccess |