FundaÃÃo de Amparo à Pesquisa do Estado do Cearà / Os arames eletrodos de aÃos inoxidÃveis martensÃticos tÃm seu emprego voltado nas soldagens de ligas ferrÃtica/martensÃticas por fornecer apropriada resistÃncia mecÃnica e à corrosÃo. Este trabalho apresenta um estudo do efeito da estrutura martensÃtica formada a baixa temperatura no metal de solda de juntas soldadas multipasse, sobre o nÃvel de tensÃes residuais, propriedades mecÃnicas e tenacidade, comparando com os resultados obtidos por soldagens convencionais. O arame eletrodo utilizado foi Fe-12%Cr-5%Ni, com temperatura de transformaÃÃo martensÃtica inferior a 200 ÂC, soldando secÃÃes de tubulaÃÃes de aÃo API 5L classe B utilizado em extraÃÃo e transporte de petrÃleo. As soldagens dos corpos de prova foram realizadas de modo automÃtico. Amostras de cada cordÃo do enchimento foram retiradas para a realizaÃÃo das anÃlises de composiÃÃo quÃmica, microdureza, caracterizaÃÃo microestrutural por microscopia Ãtica (MO) e microscopia eletrÃnica de varredura (MEV), difraÃÃo de raios-X e ensaio termo-magnÃtico. Realizando o mapeamento da textura cristalogrÃfica e determinando as variantes cristalogrÃficas da formaÃÃo da martensÃta por Electron Backscattering Diffraction (EBSD). Os resultados de tensÃes residuais mostraram que as juntas soldadas com eletrodo de baixa temperatura de transformaÃÃo martensÃtica apresentaram maiores intensidades de tensÃes residuais compressivas comparados com o eletrodo comum, e nÃo influenciaram no surgimento de textura cristalogrÃfica nos cordÃes de topo. A maior energia de soldagem influenciou significativamente no aumento da tenacidade do cordÃo e contribuiu para o surgimento de austenita revertida. / Os arames eletrodos de aÃos inoxidÃveis martensÃticos tÃm seu emprego voltado nas soldagens de ligas ferrÃtica/martensÃticas por fornecer apropriada resistÃncia mecÃnica e à corrosÃo. Este trabalho apresenta um estudo do efeito da estrutura martensÃtica formada a baixa temperatura no metal de solda de juntas soldadas multipasse, sobre o nÃvel de tensÃes residuais, propriedades mecÃnicas e tenacidade, comparando com os resultados obtidos por soldagens convencionais. O arame eletrodo utilizado foi Fe-12%Cr-5%Ni, com temperatura de transformaÃÃo martensÃtica inferior a 200 ÂC, soldando secÃÃes de tubulaÃÃes de aÃo API 5L classe B utilizado em extraÃÃo e transporte de petrÃleo. As soldagens dos corpos de prova foram realizadas de modo automÃtico. Amostras de cada cordÃo do enchimento foram retiradas para a realizaÃÃo das anÃlises de composiÃÃo quÃmica, microdureza, caracterizaÃÃo microestrutural por microscopia Ãtica (MO) e microscopia eletrÃnica de varredura (MEV), difraÃÃo de raios-X e ensaio termo-magnÃtico. Realizando o mapeamento da textura cristalogrÃfica e determinando as variantes cristalogrÃficas da formaÃÃo da martensÃta por Electron Backscattering Diffraction (EBSD). Os resultados de tensÃes residuais mostraram que as juntas soldadas com eletrodo de baixa temperatura de transformaÃÃo martensÃtica apresentaram maiores intensidades de tensÃes residuais compressivas comparados com o eletrodo comum, e nÃo influenciaram no surgimento de textura cristalogrÃfica nos cordÃes de topo. A maior energia de soldagem influenciou significativamente no aumento da tenacidade do cordÃo e contribuiu para o surgimento de austenita revertida. / The filler metal of martensitic stainless steels has its used welding of alloy ferritic / martensitic to provide suitable mechanical strength and corrosion. This research accomplishes a study of the mechanical and metallurgical properties correlate with the crystallography texture and variants selection during the martensitic transformation in the weld metal. The filler metal used was Fe-12% Cr-5% Ni, with martensitic transformation temperature less than 200ÂC, welding sections of steel pipeline API 5L grade B used in oil extraction and structure offshore. The welding of the specimens was performed automatically. Samples of each layer of filling were removed for analysis during chemical composition, microhardness, microstructural characterization by optical microscopy (OM) and scanning electron microscopy (SEM), X-ray diffraction and thermo-magnetic test. Itâs intend to accomplish a mapping of texture and variants selection of the formation of martensitic morphology by Electron Backscattering Diffraction (EBSD). The results have shown that residual stresses in welded joints filler metal of low-temperature martensitic transformation had higher compressive residual stress intensities compared to the common electrode, and did not influence the appearance of crystallographic texture on top of beads. The high heat input significantly influenced the increase toughness beads and contributed to the appearance of reverted austenite. / The filler metal of martensitic stainless steels has its used welding of alloy ferritic / martensitic to provide suitable mechanical strength and corrosion. This research accomplishes a study of the mechanical and metallurgical properties correlate with the crystallography texture and variants selection during the martensitic transformation in the weld metal. The filler metal used was Fe-12% Cr-5% Ni, with martensitic transformation temperature less than 200ÂC, welding sections of steel pipeline API 5L grade B used in oil extraction and structure offshore. The welding of the specimens was performed automatically. Samples of each layer of filling were removed for analysis during chemical composition, microhardness, microstructural characterization by optical microscopy (OM) and scanning electron microscopy (SEM), X-ray diffraction and thermo-magnetic test. Itâs intend to accomplish a mapping of texture and variants selection of the formation of martensitic morphology by Electron Backscattering Diffraction (EBSD). The results have shown that residual stresses in welded joints filler metal of low-temperature martensitic transformation had higher compressive residual stress intensities compared to the common electrode, and did not influence the appearance of crystallographic texture on top of beads. The high heat input significantly influenced the increase toughness beads and contributed to the appearance of reverted austenite.
| Identifer | oai:union.ndltd.org:IBICT/oai:www.teses.ufc.br:7332 |
| Date | 10 October 2013 |
| Creators | Wellison da Silva Tavares |
| Contributors | Hamilton Ferreira Gomes de Abreu, HÃlio Cordeiro de Miranda, Marcelo Ferreira Motta, JoÃo Marcos Alcoforado Rebello, Maria da Penha Cindra Fonseca |
| Publisher | Universidade Federal do CearÃ, Programa de PÃs-GraduaÃÃo em Engenharia e CiÃncia de Materiais, UFC, BR |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Format | application/pdf |
| Source | reponame:Biblioteca Digital de Teses e Dissertações da UFC, instname:Universidade Federal do Ceará, instacron:UFC |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0031 seconds