Previous issue date: 2014-11-03 / CNPq / Um dos principais problemas do isolamento elétrico externo é o acúmulo de contaminantes em sua superfície. A ocorrência deste evento faz com que a resistência da superfície diminua, aumentando a presença de correntes de fuga pela superfície. Entre as técnicas desenvolvidas para diminuir esse tipo de efeito, está o revestimento do isolador existente convencional (porcelana ou vidro, conforme o caso) com uma borracha de silicone que é vulcanizada à temperatura ambiente (BS). O objetivo deste trabalho foi desenvolver uma mistura de borracha de silicone/alumina trihidratada/nanosílica (BS/ATH:NS) para ser usada em revestimento de isoladores elétricos de vidro. Cargas de ATH e NS foram adicionadas à BS, produzindo uma mistura feita em diferentes proporções mássicas (79/21; 77/23 e 75/25) de BS/ATH:NS, utilizada nos revestimento dos isoladores elétricos de vidro. As cargas e os revestimentos foram caracterizados por difração de raios X (DRX), microscopia eletrônica de varredura (MEV), teste de inflamabilidade, ensaio na câmara de névoa salina, molhabilidade e avaliação da hidrofobicidade. As cargas apresentaram características morfológicas bem distintas, o que interferiu diretamente na morfologia dos revestimentos. A silanização das cargas favoreceu uma interação entre elas, assim como houve uma pequena melhora na interação das cargas com a BS. Observou-se também que no teste de inflamabilidade, os revestimentos que continham ATH, apresentaram resultados mais significativos, não havendo queima. Para os ensaios na câmara de névoa salina, o revestimento com BS/20:1 e os revestimentos com cargas silanizadas apresentaram os menores valores de corrente de fuga, o que foi comprovado com a avaliação da hidrofobicidade, na qual estes conseguiram recuperar a hidrofobicidade até HC=1 (nível de hidrofobicidade), de acordo com o guia STIR (Swedish Transmission Research Institute). / One of the main problems of external electrical isolation is due to accumulation of contaminants on its surface. The occurrence of this event causes the insulation resistance of the surface decreases, increasing the flow of leakage currents on the surface. Among the techniques developed to reduce this type of event is the coating of the conventional existing insulator (porcelain or glass, as appropriate) with a silicone rubber vulcanized at room temperature (BS). The aim of this study was to develop a mixture of silicone rubber/ alumina trihydrate/nanosílica (BS/ATH:NS) for use in coating glass electrical insulators. Loads of ATH and NS were added to BS, producing a mixture made in different mass ratios (79/21, 77/23 and 75/25) BS/ATH:NS used in the coating of glass electrical insulators. Loads and coatings were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), flammability test, measurement salt spray chamber, test of wettability and hydrophobicity. Loads showed distinct morphological features, which directly affects the morphology of the coatings. The silanization loads favored interaction among them, as there was a small improvement in the interaction of the loads with the BS. It was also observed that the flammability test, the coatings containing ATH showed more significant results, without burning. For tests of the salt spray chamber, coat with BS/20:1 and with silanized fillers had the lowest leakage current, which was confirmed by measuring the hydrophobicity, where they managed to recover the hydrophobicity HC = 1 (level of hydrophobicity) according to STIR (Swedish Transmission Research Institute) guide.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/244 |
| Date | 29 January 2018 |
| Creators | BEZERRA, Daniella Cibele. |
| Contributors | ARAÚJO, Edcleide Maria., COSTA, Ana Cristina Figueiredo de Melo., FERREIRA, Tarso Vilela., ITO, Edson Noriyuki., MÉLO, Tomás Jeferson Alves de., PAZ, Rene Anisio da. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/doctoralThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | Coordenação de Aperfeiçoamento de Pessoal de Nível Superior. |
Page generated in 0.002 seconds