Previous issue date: 2014-07-18 / Este trabalho teve como objetivo a avaliação físico-química, morfológica e estrutural
das bolsas de Policloreto de Vinila (PVC) para acondicionamento de sangue e
hemocomponentes. As amostras de bolsas plásticas Nacionais e do Exterior
utilizadas para este estudo foram selecionadas no Sistema de Dados da ANVISA -
DATAVISA entre as bolsas regularizadas junto à ANVISA. As bolsas constituídas de
PVC foram caracterizadas por Espectroscopia na Região de Infravermelho com
Transformada de Fourier (FTIR), Difração de Raios X (DRX), Microscopia Óptica
(MO), Microscopia Eletrônica de Varredura (MEV)/ Espectroscopia por Energia
Dispersa de Raios X (EDS), Microscopia de Força Atômica (MFA) e Ensaios
Mecânicos (Tração). As análises foram realizadas no Laboratório de
Desenvolvimento e Avaliação de Biomateriais (CERTBIO). De acordo com os
resultados observados no ensaio de FTIR, pode-se afirmar que todos os
componentes apresentam grupos funcionais semelhantes. No DRX foi observado
que as amostras apresentaram um perfil de material com caráter semicristalino. Na
MO e MEV observou-se um lado mais liso e outro mais rugoso com algumas
irregularidades na superfície da amostra. Conforme o ensaio de EDS, os elementos
químicos identificados, bem como a concentração dos mesmos, demonstrou que as
bolsas seguem um mesmo critério de composição. Baseado nos resultados de
ensaios mecânicos para ambos fabricantes, as bolsas de sangue sem
anticoagulante apresentaram menor deformação em relação as bolsas de sangue
com anticoagulante. Todas as bolsas apresentaram comportamento de material
viscoelástico. Desta forma, pode-se concluir que todos os ensaios de caracterização
utilizados neste trabalho foram relevantes para avaliação da qualidade das bolsas
plásticas para acondicionamento de sangue e hemocomponentes existentes no
mercado, considerando os requisitos gerais e específicos estabelecidos nas normas
e legislações vigentes. / This research has the objective the physical chemical, morphological and structural
evaluation of Polyvinyl Chloride (PVC) bags for blood filling and hemocomponentes.
The samples from national and imported blood bags used for this research were
selected through ANVISA database from blood bags regularly released by that. The
PVC blood bags were characterized by Fourier transform Infrared (FTIR), X-ray
Diffraction (XRD), optical microscopy (OM), scanning electron microscopy (SEM),
energy dispersed spectroscopy X-ray (EDS), Atomic Force Microscopy (AFM) and
Mechanical Testing. The analyses were performed on Biomaterial development and
evaluation lab (CERTBIO). On Fourier transform Infrared (FTIR) it was observed that
all components show chemical similarity. On XRD was noticed that the samples have
showed a semi crystalline characteristics. On OM and SEM it was noticed that the
sample has a smooth side and other with sprinkles on surface. ON EDS assay it was
observed conformity on chemical compounds identified as well as on their strength. It
demonstrates that blood bags follow the same composition criteria. Based on
mechanical tests results for both manufacturers, the blood bags without
anticoagulant showed less deformation compared to blood bags with anticoagulant.
All bags showed viscoelastic material behavior. Thus, we can conclude that all
characterization tests used in this study were relevant to assessing the quality of the
bags that are used as containers of blood and its components existing on the market,
considering the general and specific requirements established in rules and
regulations.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/383 |
| Date | 13 April 2018 |
| Creators | FERREIRA, Leila Aparecida Alvim de Paula. |
| Contributors | FOOK, Marcus Vinícius Lia., FOOK, Sayonara Maria Lia., SANTOS, Patrícia Tatiana Araújo dos. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds