Previous issue date: 2014-07-16 / O polietileno de ultra alto peso molecular (PEUAPM) é um polímero com
excelentes propriedades físicas e mecânicas tendo como mais notáveis a sua
inércia química, a lubricidade, resistência impacto e resistência a abrasão.
Exibe um papel relevante no sucesso na Artroplastia Total de Joelho (ATJ) e
Artroplastia Total de Quadril (ATQ). A Artroplastia se caracteriza pela
substituição da articulação natural por uma articulação artificial. As articulações
artificiais são formadas por um conjunto de componentes, sendo fabricados de
matéria prima metálica ou cerâmica e um componente, normalmente feito em
PEUAPM, que é interposto entre componentes metálicos. Alguns fatores
contribuem para um maior desgaste do componente de polietileno. Os
componentes fabricados em polietileno PEUAPM não possuem
fotoestabilizadores. E em inspeções realizadas em fabricantes e distribuidores
destes produtos foi observado que durante seu processamento fabril e
comercialização eles não são adequadamente protegidos da iluminação direta.
As características consideradas importantes para o desempenho in vitro destes
dispositivos estão definidas em normas técnicas, mas muitas destas normas
somente recomendam determinados requisitos considerados importantes do
ponto de vista técnico. Atualmente a área de materiais de uso em saúde
trabalha em regulamentos que visam instituir os requisitos mínimos para
registro de implantes ortopédicos. Desta forma, este trabalho propôs avaliar as
possíveis alterações de componentes fabricados em polietileno de ultra alto
peso molecular utilizados em procedimentos cirúrgicos de artroplastia e joelho
e quadril, exposto a radiação ultravioleta. O trabalho foi dividido em 4 grupos:
grupo 1 (material não exposto a UV); grupo 2 (material exposto a UV por 1h);
grupo 3 (material exposto a UV por 24h) e grupo 4 (material exposto a UV por
48h). Todas as amostras foram caracterizadas por Difração de Raio X (DRX),
Espectroscopia de Absorção de Infravermelho por Transformada de Fourier
(FTIR), Microscopia Ótica (MO), Microscopia Eletrônica de Varredura (MEV)
com mapeamento por EDS e Microscopia de Força Atômica (AFM) com o
intuito de avaliar as possíveis degradações do PEUAPM submetidos a radiação
UV. Os resultados demonstraram que a exposição do polímero a radiação UV
em todos os tempos testados neste trabalho promoveu alterações nas
amostras, pois foi observado, principalmente, nos ensaios de DRX e EDS que
ocorreu respectivamente, um discreto aumento da cristalinidade do material e
diminuição no percentual de oxigênio. Desta forma, pode-se concluir que o
aumento da cristalinidade pode, pela ação da radiação UV, afetar nas
propriedades do material contribuindo para o aumento do desgaste e
diminuição do tempo de vida útil do implante. / The polyethylene, ultra high molecular weight (UHMWPE) is a polymer with
excellent physical and mechanical properties with the most notable its chemical
inertness, lubricity, impact resistance and abrasion resistance. Displays a
relevant role in the successful Total Knee Arthroplasty (TKA) and Total Hip
Arthroplasty (THA). The arthroplasty is characterized by replacement of the
natural joint with an artificial joint. Artificial joints are formed by a set of
components, being manufactured from metal or ceramic raw material and a
component normally done in UHMWPE, which is interposed between the metal
components. Some factors contribute to increased wear of the polyethylene
component. Components manufactured in polyethylene UHMWPE not have
photostabilizers. And inspections on manufacturers and distributors of these
products was observed that during its industrial processing and marketing they
are not adequately protected from direct light. Characteristics considered
important for the in vitro performance of these devices are set in technical
standards, but many of these standards only recommend certain requirements
considered important from a technical standpoint. Currently the area of
materials for use in healthcare working on regulations that seek to establish the
minimum requirements for registration of orthopedic implants. Thus, this study
aimed to evaluate the possible changes of components manufactured in
polyethylene, ultra high molecular weight used in surgical procedures and knee
arthroplasty and hip, exposed to ultraviolet radiation. The work was divided into
4 groups: group 1 (material not exposed to UV); group 2 (material exposed to
UV for 1 h); group 3 (material exposed to UV for 24 h) and group 4 (material
exposed to UV for 48 h). All samples were characterized by X-Ray Diffraction
(XRD), Absorption Spectroscopy Fourier Transform Infrared (FTIR), optical
microscopy (OM), scanning electron microscopy (SEM) with EDS mapping and
Atomic Force Microscopy (AFM) in order to evaluate the possible degradation of
UHMWPE subjected to UV radiation. The results showed that exposure of the
polymer to UV radiation at all times tested in this study modified the samples, it
was observed mainly in the experimental XRD and EDS which occurred
respectively a slight increase in crystallinity and decrease in the percentage
oxygen. Thus, it can be concluded that the increase in crystallinity can by the
action of UV radiation, affect the material properties contributing to increased
wear and reduced useful life of the implant.
| Identifer | oai:union.ndltd.org:IBICT/oai:localhost:riufcg/384 |
| Date | 13 April 2018 |
| Creators | RIBEIRO, Márcia Cristina de Moraes Reis. |
| Contributors | FOOK, Marcus Vinícius Lia., RIGO, Eliana Cristina da Silva., SANTOS, Patrícia Tatiana Araújo dos. |
| Publisher | Universidade Federal de Campina Grande, PÓS-GRADUAÇÃO EM CIÊNCIA E ENGENHARIA DE MATERIAIS, UFCG, Brasil, Centro de Ciências e Tecnologia - CCT |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Biblioteca de Teses e Dissertações da UFCG, instname:Universidade Federal de Campina Grande, instacron:UFCG |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0025 seconds