Previous issue date: 2017-08-30 / Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq) / Ao longo das duas últimas décadas, a contribuição da manufatura aditiva passou da confecção de um mero protótipo de um produto, no início de seu desenvolvimento, para a confecção de qualquer produto direto, presente em todos os setores industriais. Com este avanço, diferentes tecnologias da manufatura aditiva surgiram com o intuito de melhorar alguns parâmetros de produção. Neste meio, a tecnologia de impressão tridimensional 3DP, por consequência de suas várias características intrínsecas, se destaca para atender o setor biomédico, através da técnica de biomodelagem, que contribuem imensamente de forma didática e prática para a performance de cirurgias. Porém, há algumas limitações finais nas peças obtidas por esta tecnologia que devem ser contornadas, focando-se no tratamento adicional necessário destas peças, o pós-processamento, de modo a aprimorá-las, conferindo então sucesso ao destino destas. Neste trabalho, adotou-se a tecnologia de manufatura aditiva 3DP para estudar como a adição de diferentes agentes infiltrantes influenciam no acréscimo de densidade aparente e resistência mecânica de amostras feitas de componentes de gesso, constituídas por corpos de prova cilíndricos e prismáticos, de modo a simular a melhor composição para biomodelos. Para isto, o pós-processamento foi dividido em duas etapas. Na primeira etapa, foram aplicados separadamente nas amostras, quatro tipos de adesivos à base de etilcianocrilato, por gotejamento, e um à base de epóxi, por moldagem com pá. Já na segunda etapa, foram aplicados nas amostras, também separadamente, quatro tipos de adesivos à base de etilcianocrilato, por gotejamento e banho de imersão, e um à base de epóxi, por moldagem com pá. Além dos métodos de aplicação dos adesivos, as duas etapas se diferem também pelos binders utilizados para constituírem as amostras à base de gesso. Para ambas etapas, obteve-se o melhor resultado com o adesivo de cianocrilato de baixíssima viscosidade, capaz de provocar maiores variações de densidade aparente às amostras, além de maiores acréscimos de resistência. / Over the past two decades, the contribution of additive manufacturing has shifted from a mere prototype of a product at the beginning of its development to the production of any direct product present in all industrial sectors. With this advance, different technologies of the additive manufacturing appeared with the intention to improve some parameters of production. In this environment, three-dimensional printing 3DP technology, due to its various intrinsic characteristics, stands out to serve the biomedical sector through the biomodelling technique, which contribute immensely in a didactic and practical way for the performance of surgeries. However, there are some final limitations in the parts obtained by this technology that must be improved, focusing on the necessary additional treatment of these parts, the post-processing, in order to upgrade them, thus giving success to their destination. In this study, 3DP additive manufacturing technology was adopted to study how different infiltrating agents influence the increase in apparent density and mechanical strength of samples made of gypsum components, constituted by cylindrical and prismatic specimens, in order to simulate the best composition for biomodels. For this, the post-processing was divided in two stages. In the first stage, separately, four types of ethylcyanoacrylate-based adhesives were applied on the samples by dripping, and one epoxy-based adhesive was applied by shovel molding. In the second stage, also separately, four types of ethylcyanocrylate based adhesives were applied in the samples, by dripping and by dipping, and the epoxy-based, by shovel molding. Besides the adhesive application methods, the two stages also differ from the binders used to constitute the gypsum-based samples. For both stages, the best result was obtained by the cyanoacrylate adhesive with very low viscosity, capable of causing greater variations of apparent density and additions of strength to the samples.
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unesp.br:11449/152037 |
| Date | 30 August 2017 |
| Creators | Mello, Silvia Teixeira de [UNESP] |
| Contributors | Universidade Estadual Paulista (UNESP), Tokimatsu, Ruis Camargo [UNESP] |
| Publisher | Universidade Estadual Paulista (UNESP) |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | English |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Source | reponame:Repositório Institucional da UNESP, instname:Universidade Estadual Paulista, instacron:UNESP |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | -1, -1 |
Page generated in 0.0031 seconds