Orientador: Lourenço Correr Sobrinho / Dissertação (mestrado) - Universidade Estadual de Campinas, Faculdade de Odontologia de Piracicaba / Made available in DSpace on 2018-08-27T03:18:45Z (GMT). No. of bitstreams: 1
Moreno_MarinaBarretoPereira_M.pdf: 912245 bytes, checksum: 9df1e682d509df817a27377fe24b3eef (MD5)
Previous issue date: 2015 / Resumo: A polimerização adequada de cimentos resinosos é fundamental para obter excelentes propriedades físico-mecânicas. Fatores relacionados à cerâmica e ao próprio cimento podem influenciar a passagem de luz, reduzindo a fotoativação e alterando o grau de polimerização dos cimentos. O propósito neste estudo foi avaliar a dureza Knoop após 15 min ou 24h de diferentes cores de cimento resinoso fotoativado, com ou sem a interposição da cerâmica, em diferentes profundidades. Amostras com 5 mm de diâmetro e 1 mm de espessura do cimento resinoso Variolink Veneer (Ivoclar Vivadent) nas cores HV+1, HV+2, HV+3, MV0, LV-1, LV-2 e LV-3, foram feitas em um molde de elastômero, cobertas com uma tira de poliéster e por um disco de cerâmica IPS e.max Press (Ivoclar Vivadent) na espessura de 0,7 mm e fotoativadas por 20 segundos usando o LED Radii-cal (SDI Limited), com 1.200 mW/cm2. O cimento resinoso foi transversalmente desgastado e submetido ao teste de dureza Knoop usando o aparelho HMV 2 (Shimadzu), com carga de 50g aplicada por 15 segundos, 15 min após a fotoativação e após armazenagem a 37o C por 24 horas. Cinco penetrações foram feitas na secção transversal a 100 e 700 µm da superfície de topo, sendo que vinte amostras foram confeccionadas para cada cor do cimento resinoso Variolink Veneer em cada período de armazenagem. Os dados foram submetidos à Análise de Variância em esquema de parcelas subdivididas (cor, tempo pós-ativação, modo de ativação e profundidade), seguido pelo teste de Tukey post hoc (? = 0,05). Significante diferença para a cor (p<0,0001), modo de ativação (p<0,001), tempo pós-ativação (p<0,0001) e profundidade (p<0,0001) foi detectada. Nenhuma diferença significante foi detectada entre as interações (p>0,05), exceto para a interação cor x tempo pós-ativação (p<0,0045) e modo de ativação x tempo pós-ativação (p<0,0003). A cor do cimento resinoso e a ativação indireta tiveram significante efeito na dureza Knoop. Houve um aumento significante na dureza Knoop, após 24 horas para todas as cores do cimento resinoso. A profundidade influenciou significantemente na dureza Knoop / Abstract: An adequate polymerization of resin cements is essential to obtain excellent physical and mechanical properties. Factors related to the ceramic and cement itself can influence the passage of light, decreasing the light curing and the degree of polymerization of the cement. The aim of this study was to evaluate the Knoop hardness number of different shades of resin cement light-cured either through or without the ceramic restoration and tested after 15 min or 24 h at different depths. The specimens with 5.0 mm in diameter and 1.0 mm thickness of the luting resin cement Variolink Veneer (Ivoclar Vivadent) in the HV+1, HV+2, HV+3, MV0, LV-1, LV-2 and LV-3 shades, were made in the elastomer mold, covered with a mylar strip and ceramic IPS e.max Press (Ivoclar Vivadent) disc in the thickness 0.7 mm and light-activated for 20 seconds using a LED Radii-cal (SDI Limited), with 1200 mW/cm2. The resin cement specimens were transversely wet-flattened and submitted to Knoop hardness using HMV 2 microhardness tester (Shimadzu), with a load of 50g applied for 15 seconds, 15 min after photoactivation and after storage at 37o C for 24 hours. Five indentations were made in the cross-sectional area at 100 and 700 µm from the top surface, being that twenty specimens were made for each shades of Variolink Veneer in each stored time. Data were submitted to ANOVA split-plot design (shade, post-cure time, mode of activation, and depth), followed by Tukey post hoc test (? = 0.05). The mean values of Knoop hardness are shown in Table 1. Significant differences for shade (p<0.0001), mode of activation (p<0.001), post-cure time (p<0.0001) and depth (p<0.0001) were detected. There was not significance in the interactions (p>0.05), except for shade x post-cure time (p<0.0045) and mode of activation x post-cure time (p<0.0003). The resin cement shade and indirect activation had a significant effect on the Knoop hardness. There was a significant increase in Knoop hardness after 24 h in all cements shades. The depth influenced significantly on the Knoop hardness / Mestrado / Materiais Dentarios / Mestra em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/289558 |
| Date | 27 August 2018 |
| Creators | Moreno, Marina Barrêto Pereira, 1989- |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Correr Sobrinho, Lourenço, 1960-, Borges, Gilberto Antonio, Consani, Simonides |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba, Programa de Pós-Graduação em Materiais Dentários |
| Source Sets | IBICT Brazilian ETDs |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 31 f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0138 seconds