This thesis is focused on carbide ceramics synthesis, more specifically on the synthesis of a Ti2AlC MAX Phase carbide using solution chemistry rather than powder metallurgy. Chloride and nitrate precursors have been used as a source of metals and citric acid as a source of carbon for carbothermal reduction and as a complexing agent. A new route of precursor synthesis has been developed based on peroxo-titanic acid, which helps retain aluminium. The syntheses were performed using the SPS facility to ensure high heating rates. Al4C3 and TiC carbides and their mixtures were prepared successfully. However, the Ti2AlC phase was not synthesized under used conditions. The phase composition, structure and grain sizes of the samples were investigated by powder X-ray diffraction, X-ray fluorescence and electron microscopy. The contents of carbon in the precursors were determined by thermogravimetric analysis.
| Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:434179 |
| Date | January 2020 |
| Creators | Nižňanský, Matěj |
| Contributors | Tyrpekl, Václav, Vilémová, Monika |
| Source Sets | Czech ETDs |
| Language | English |
| Detected Language | English |
| Type | info:eu-repo/semantics/masterThesis |
| Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0017 seconds