The master thesis is dealing with characterization of the structure and properties of the YSZ thermal barrier coating deposited by water hybrid plasma spray technology on the CoNiCrAlY bond coats modified by using electron beam and vacuum annealing. Deposition of the bond coats was performed via high velocity oxy-fuel technology and cold spray. In case of experimental evaluation, the microstructure and chemical composition of the ceramic top coat deposited with powder and suspension feedstock was analyzed. The same analysis procedure was used also for bond coats after electron beam remelting by using two sets of parameters. Furthermore, the changes in microstructure and chemical composition of the remelted and annealed bond coats was evaluated. Eventually, the micromechanical properties of the top coats and the bond coats were measured. The ceramic top coats deposited with powder feedstock exhibited the structure composed by splats, while the top coats deposited in form of suspension showed fine structure with columnar grains. The dendritic structure was observed on remelted bond coats. The annealing process had an influence on the structure in form of coarsened phases and the chemical composition was changed due to diffusion of the elements.
Identifer | oai:union.ndltd.org:nusl.cz/oai:invenio.nusl.cz:400863 |
Date | January 2019 |
Creators | Slavíková, Barbora |
Contributors | Jan, Vít, Dlouhý, Ivo |
Publisher | Vysoké učení technické v Brně. Fakulta strojního inženýrství |
Source Sets | Czech ETDs |
Language | Czech |
Detected Language | English |
Type | info:eu-repo/semantics/masterThesis |
Rights | info:eu-repo/semantics/restrictedAccess |
Page generated in 0.0117 seconds