In the last years, intensive research on new tunable solid state laser materials has been carried out. For the spectral range from 1300 to 1600 nm the Cr4+ ion seems to be the most promising laser-ion. In order to meet the the demand of broad-band devices, we employed the Cr4+ doped YAG crystal fibers with high optical quality thin films design and coating (high index material TiO2, low index material SiO2) to achieve the development of high efficiency crystal fiber lasers.
In this thesis, crystal fiber was used as the laser gain medium, and coated with optical thin films at both end faces (input face 900-1100 nm AR and 1300-1600 nm HR; output face 1300-1600 nm HR) as the laser cavity to reduce the loss and promote laser efficiency. During the experiment, we tried to optimize the coating conditions to acquire high density, stable index and low absorption coefficient thin films. With different thin film thickness and stacking designs, the electric field distribution was designed to be away from the laser interface and high index region to increase the laser-induced damage threshold and lifetime for high power pumping. In addition, CaO and Cr2O3 were deposited on Cr4+:YAG source rods before the laser-heated-pedestal growth to increase CaO and Cr2O3 doping concentration for higher fluorescence efficiency and signal saturation power.
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0709104-135520 |
| Date | 09 July 2004 |
| Creators | Lin, Yu-Hsien |
| Contributors | Chung-Wen Lan, Tao-Yuan Chang, Pou-Yan Shen, Yen-Sheng Lin, Sheng-Lung Huang |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | Cholon |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0709104-135520 |
| Rights | not_available, Copyright information available at source archive |
Page generated in 0.0017 seconds