This research project is a preliminary investigation of the effect of SiC abrasive
breakdown on the wear rate of a WC-12wt%Co mining alloy. Wear tests were
carried out on a two body-sliding wear apparatus under (a) “Ideal” (replacing the
SiC paper periodically to ensure continual exposure to fresh abrasives), (b) “No
debris” (removing the wear debris periodically) and (c) “With debris” (retaining
the wear debris for the entire wear test) wear conditions. The WC-12wt%Co
specimens and SiC abrasive grits were examined before and after the wear tests
using optical, stereo and electron microscopy.
As wear progressed, the SiC abrasives blunted thereby increasing the
abrasive/specimen contact area, resulting in a reduction in the WC-12wt%Co
wear rate. Wear debris clogging the interstices between the abrasive grits caused a
further reduction in the WC-12wt%Co wear rate by adding to the
abrasive/specimen contact area already created by blunting. Increasing the applied
load resulted in an increase in the WC-12wt%Co wear rate under “Ideal” wear
conditions. Under the remaining wear conditions, the increased load resulted in a
faster deterioration of the SiC grits. The dominant wear mechanisms under all
conditions are characterized by hard abrasive wear that caused extensive
grooving, Co binder extrusion and cracking and fragmentation of WC grains.
| Identifer | oai:union.ndltd.org:netd.ac.za/oai:union.ndltd.org:wits/oai:wiredspace.wits.ac.za:10539/4982 |
| Date | 25 June 2008 |
| Creators | Mabhali, Luyolo Andrew Baxolise |
| Source Sets | South African National ETD Portal |
| Language | English |
| Detected Language | English |
| Type | Thesis |
| Format | 13121 bytes, 7481595 bytes, 15365 bytes, 7650 bytes, 7587974 bytes, 4477 bytes, 20262 bytes, 9773 bytes, 314928 bytes, 111521 bytes, 13390 bytes, 5845 bytes, 11264 bytes, 35095 bytes, 36953 bytes, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf, application/pdf |
Page generated in 0.0049 seconds