Ti2AlC coatings have been fabricated by cold-spray deposition. The microstructure evolution as a function of basic spray parameters temperature and pressure onto AA6060 aluminium alloy and 1.0037 steel substrates has been studied. Adherent and dense 50–80 μm thick Ti2AlC coatings were deposited on soft AA6060 substrates under gas temperature and pressure of 600 °C and 3.4 MPa, respectively, whilst comparable results were obtained on harder 1.0037 steel by using higher temperature (800 °C) and pressure (3.9 MPa).
| Identifer | oai:union.ndltd.org:UPSALLA1/oai:DiVA.org:liu-92686 |
| Date | January 2013 |
| Creators | Rech, S, Surpi, A, Vezzu, S, Patelli, A, Trentin, A, Glor, J, Frodelius, Jenny, Hultman, Lars, Eklund, Per |
| Publisher | Linköpings universitet, Tunnfilmsfysik, Linköpings universitet, Tekniska högskolan, Linköpings universitet, Tunnfilmsfysik, Linköpings universitet, Tekniska högskolan, Linköpings universitet, Tunnfilmsfysik, Linköpings universitet, Tekniska högskolan, Veneto Nanotech ScpA, Italy, Veneto Nanotech ScpA, Italy, Veneto Nanotech ScpA, Italy, Veneto Nanotech ScpA, Italy, Veneto Nanotech ScpA, Italy, Sandvik Mat Technology, Sweden, Elsevier |
| Source Sets | DiVA Archive at Upsalla University |
| Language | English |
| Detected Language | English |
| Type | Article in journal, info:eu-repo/semantics/article, text |
| Format | application/pdf |
| Rights | info:eu-repo/semantics/openAccess |
| Relation | Vacuum, 0042-207X, 2013, 94, s. 69-73 |
Page generated in 0.0027 seconds