Composite polymer particles were made of two or more polymers. If these polymers are incompatible, the particles after polymer phase segregation exhibit complex morphologies which determine their properties and applications. Such particles may have applications in both academia and industry.
In this work, polystyrene (PS)/ poly(2-cinnamoyloxyethyl methacrylate) (PCEMA) and poly(acetyloxyethyl methacrylate) (PAEMA)/PCEMA composite polymer particles are prepared by the evaporation of toluene from PS/PCEMA/toluene and PAEMA/PCEMA/toluene droplets dispersed in an aqueous solution containing surfactants. The surfactants used for the two systems are poly(glyceryl methacrylate)100-block-poly(2-cinnamoyloxyethyl methacrylate)15 (PGMA100-b-PCEMA15) and poly(glyceryl methacrylate)300-block-poly(2-cinnamoyloxyethyl methacrylate-ran-acetyloxyethyl methacrylate)37 (PGMA300-b-P(CEMA-ran-AEMA)37), respectively, for the PS/PCEMA and the PAEMA/PCEMA systems. The morphologies of the PS/PCEMA and PAEMA/PCEMA composite particles are analyzed by transmission electron microscopy (TEM), atomic force microscopy (AFM), and dynamic light scattering (DLS). The results indicate that the particles are polydisperse and of nanometer size. For the PAEMA/PCEMA particles, the preferred morphology is hemisphere, while for the PS/PCEMA system the morphology is a mixture of acorn and occluded core-shell. Based on Gibbs free energy theory, and knowing the corresponding surface tensions and interfacial tensions, the thermodynamic equilibrium morphologies for both kinds of composite particles were found. Due to the uncertainty during measurements and calculations, and the influence of kinetic factors, the theoretical predictions agreed only partially with the experimental observations. / Thesis (Master, Chemistry) -- Queen's University, 2008-08-27 12:16:37.142
| Identifer | oai:union.ndltd.org:LACETR/oai:collectionscanada.gc.ca:OKQ.1974/1374 |
| Date | 27 August 2008 |
| Creators | Wang, Nan |
| Contributors | Queen's University (Kingston, Ont.). Theses (Queen's University (Kingston, Ont.)) |
| Source Sets | Library and Archives Canada ETDs Repository / Centre d'archives des thèses électroniques de Bibliothèque et Archives Canada |
| Language | English, English |
| Detected Language | English |
| Type | Thesis |
| Format | 4090793 bytes, application/pdf |
| Rights | This publication is made available by the authority of the copyright owner solely for the purpose of private study and research and may not be copied or reproduced except as permitted by the copyright laws without written authority from the copyright owner. |
| Relation | Canadian theses |
Page generated in 0.0019 seconds