Previous issue date: 2005 / Resumo: O objetivo deste estudo foi avaliar o efeito da variação da densidade de energia na resistência da união de compósitos odontológicos à estrutura dental, a partir da interação intensidade de luz versus tempo de exposição, com diferentes fontes de luz. Foram confeccionados 260 preparos cavitários classe V em incisivos bovinos, separados em 26 grupos (n = 10) que, na seqüência, foram restaurados com dois compósitos de marcas comerciais diferentes (Z250 - 3M/ESPE e Esthet-X - Dentsplay). As cavidades foram padronizadas (formato de ¿caixa com expulsividade emergente¿ configurando um troncocônico tridimensional com dimensões de 4 x 4 x 2,4 mm) e obtidas com ponta diamantada tronco-cônica 3131 (KG-Sorensen) com ângulo aproximado de 4o, montada em caneta de alta rotação adaptada a uma mesa de coordenadas. As restaurações foram confeccionadas em incremento único sendo a fotoativação realizada com aparelho de lâmpada halógena ou LED emitindo irradiância inicial de 700mW/cm2 e 600mW/cm2 respectivamente. Após o procedimento restaurador, seccionou-se longitudinalmente a coroa, respeitando-se o plano
mésio-distal e, em seguida, realizou-se desgaste cuidadoso, via câmara pulpar, da parede axial da cavidade restaurada, com a finalidade de expor totalmente a base menor da restauração. Os corpos-de-prova foram levados à máquina de ensaio universal Instron (modelo 4411) para realização do teste de push-out. A velocidade do teste foi de 0,5mm/min até a ruptura da união e os dados coletados em Kgf foram transformados em MPa e submetidos a análise de variância e comparados pelo teste de Tukey (5%). Os resultados mostraram que o compósito Z250 apresentou médias de resistência da união estatisticamente superiores (p<0,05) tanto para o aparelho de lâmpada halógena quanto para o LED em todas as simulações clínicas estudadas, quando comparado ao Esthet-X. O aparelho LED, para o compósito Z250, proporcionou valores de resistência da união
estatisticamente superiores (p<0,05) quando comparados com à lâmpada halógena e para o Esthet-X isso não foi observado. De modo geral, a densidade de energia disponível durante a fotoativação mostrou ter maior influência na resistência da união que intensidade de luz em restaurações com alto Fator-C / Abstract: The aim of this study was to evaluate the effect of the maintenance of the energy density by the light intensity and exposure time modulation, with different light sources, on the bond strength of dental composites to tooth structure. Two hundred and sixty expulsive box shaped Type V cavities (4 x 4 x 2.4mm) had been prepared in selected bovine incisors, which were divided in 26 groups (n=10) restored immediately with two
composites of different brands (Z250 - 3M/ESPE and Esthet-X - Dentsply). Cavities were standardized (trapezoidal 3-D box shaped expulsive cavity with 4x4x2.4mm) and prepared with truncated diamond bur # 3131 (KG-Sorensen) with 4 degrees, mounted in air turbine adapted to a specific device. The restorations were bulk filled and light cured with halogen light or LED emitting irradiance of 700mW/cm2 and 600mW/cm2 respectively. After the
restorative procedure, the specimens were longitudinally sectioned, respecting the mesiodistal plan. The axial wall of the cavities was ground via pulp chamber to completely expose the smaller base of the restoration. The samples were submitted to push-out test in a universal tester machine Instron (model 4411) with crosshead speed of 0.5mm/min. The data in Kgf were transformed in MPa, which were submitted to ANOVA and means compared by Tukey's test (5%). The results had shown that the composite Z250 presented higher bond strength means compared to Esthet-X in all tested conditions (p< 0.05), as with the halogen light as with LED. Moreover, for the composite Z250, light-curing with LED resulted in higher bond strength compared to halogen light (p< 0.05), what was not verified for Esthet-X. In general, the energy density supplied during light curing showed to be more
important than light intensity in the bond strength of restorations with high C-factor / Mestrado / Materiais Dentarios / Mestre em Materiais Dentários
| Identifer | oai:union.ndltd.org:IBICT/oai:repositorio.unicamp.br:REPOSIP/288130 |
| Date | 25 February 2005 |
| Creators | Segreto, Dario Raimundo |
| Contributors | UNIVERSIDADE ESTADUAL DE CAMPINAS, Sinhoreti, Mário Alexandre Coelho, 1969-, Piva, Evandro, Carrilho, Marcela Rocha de Oliveira |
| Publisher | [s.n.], Universidade Estadual de Campinas. Faculdade de Odontologia de Piracicaba |
| Source Sets | IBICT Brazilian ETDs |
| Language | Portuguese |
| Detected Language | Portuguese |
| Type | info:eu-repo/semantics/publishedVersion, info:eu-repo/semantics/masterThesis |
| Format | 95f. : il., application/pdf |
| Source | reponame:Repositório Institucional da Unicamp, instname:Universidade Estadual de Campinas, instacron:UNICAMP |
| Rights | info:eu-repo/semantics/openAccess |
Page generated in 0.0036 seconds