The thermal and mechanical properties of the Mg-based bulk metallic glasses are reported in this thesis. The original ingots were prepared by arc melting and induction melting. The thermal and mechanical properties of the Mg-based bulk metallic glasses are reported in this thesis. The original ingots were prepared by arc melting and induction melting. The Mg65Cu25Gd10 and Mg65Cu15Ag10Gd10 bulk metallic glasses with different diameters from 3 to 6 mm were successfully fabricated by conventional copper mold casting in an inert atmosphere.
The Mg65Cu25Gd10 bulk metallic glass shows the high glass forming ability and good thermal stability. However, the addition of Ag in the Mg65Cu15Ag10Gd10 alloy degrades the thermal stability. Based on the DSC results, the supercooled liquid region
| Identifer | oai:union.ndltd.org:NSYSU/oai:NSYSU:etd-0727106-113505 |
| Date | 27 July 2006 |
| Creators | Chen, Hai-ming |
| Contributors | Chih-ching Huang, Ker-chang Hsieh, Shian-ching Jang |
| Publisher | NSYSU |
| Source Sets | NSYSU Electronic Thesis and Dissertation Archive |
| Language | English |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | http://etd.lib.nsysu.edu.tw/ETD-db/ETD-search/view_etd?URN=etd-0727106-113505 |
| Rights | off_campus_withheld, Copyright information available at source archive |
Page generated in 0.0015 seconds