Autogenous shrinkage is of concern in high performance concrete mixtures, when specific properties like strength and durability are enhanced. Factors like low watercement ratio, low porosity and increased hydration kinetics which are associated with high performance concrete mixtures are also responsible for the development of autogenous shrinkage. With about two decades of research into autogenous shrinkage, uncertainties still exist with testing procedure, effect of supplementary cementitious materials, modelling and prediction of autogenous shrinkage. The primary focus of this study is to understand mechanisms which have been postulated to cause autogenous shrinkage like chemical shrinkage and self desiccation. In addition, this study has considered properties like porosity and internal empty voids in the analysis of the causes of bulk volume deformations of the cementitious paste systems with and without mineral admixtures. The study begins with an experimental investigation of chemical shrinkage in hydrating cementitious paste systems with the addition of fly ash, slag and silica fume using the test method recently accepted by the ASTM. This was followed by the experimental investigation of autogenous shrinkage in cementitious paste. The autogenous shrinkage in paste mixtures is studied from an early age (~1.5 hours after addition of water) for cementitious systems at a water-cementitious ratio of 0.32 (w/c 0.25 for limited mixture proportions). A non-contact measurement method using eddy current sensors were adopted. The hydration mechanism of the cementitious paste systems was then modelled using CEMHYD3D, which is a 3 dimensional numerical modelling method successfully used to study, simulate and present the hydration developments in cementitious systems. Properties like chemical shrinkage, degree of hydration, total porosity and free water content; all of which have been obtained from the CEMHYD3D simulation have been cross correlated with the experimental results in order to more comprehensively understand the mechanism contributing to bulk volume change under sealed conditions. The experimental investigations are extended to study the development in concrete with and without mineral admixtures (i.e., silica fume, fly ash and slag). Self desiccation driving the development of autogenous shrinkage has been used extensively across literature but as an alternative the author has proposed using internal drying factor in modelling autogenous shrinkage. The "internal drying factor" is described as the ratio of the empty voids (due to chemical shrinkage) to the total porosity at any point of time of hydration. Independent of the mixture proportions, a linear trend was observed between the autogenous shrinkage strain and increase in internal drying factor. Thus the internal drying factor could be incorporated into semiempirical models while attempting to predict autogenous shrinkage. An increase in the compressive strength of matured concrete at 1 year had a strong correlation to the observed autogenous shrinkage strains irrespective of the cementitious system. It is believed this could be because of the increase in gel-space ratio which is intern linked to the degree of hydration and porosity of the microstructure. The author has obtained strong evidence that the micro-structural changes associated with high strength and durable concrete have a direct impact on the autogenous shrinkage of concrete. Hence, the author suggests that autogenous shrinkage should be investigated and allowable values be stipulated as design criterion in structures that use high strength-high performance concrete.
| Identifer | oai:union.ndltd.org:ADTP/258767 |
| Date | January 2009 |
| Creators | Rajayogan, Vinod, Engineering & Information Technology, Australian Defence Force Academy, UNSW |
| Publisher | Awarded by:University of New South Wales - Australian Defence Force Academy. Engineering & Information Technology |
| Source Sets | Australiasian Digital Theses Program |
| Language | English |
| Detected Language | English |
| Rights | http://unsworks.unsw.edu.au/copyright |
Page generated in 0.0015 seconds