Simplified mechanical loading paths, which represent more complex loading paths observed during penetration, were investigated using a triaxial chamber and a high-strength concrete. Objectives were to determine the effects that stress/strain (load) paths had on the material’s unconfined (UC) residual strength. The loading paths included hydrostatic compression (HC), uniaxial strain in compression (UX), and uniaxial strain load biaxial strain unload (UXBX). The experiments indicate that load paths associated with non-visible microstructural damage were HC and UX, which produced minimal impact on the residual UC strength (<30%), while the load paths associated with visible macro-structural damage were UXBX, which significantly reduced the UC strength (>90%). The simplified loading paths were also investigated using a material model driver code that was fit to a widely used Department of Defense material model. Virtual experiment data revealed that the material model investigated overestimated material damage and produced poor results when compared to experimental data.
| Identifer | oai:union.ndltd.org:MSSTATE/oai:scholarsjunction.msstate.edu:td-4798 |
| Date | 25 November 2020 |
| Creators | Vankirk, George Harlan |
| Publisher | Scholars Junction |
| Source Sets | Mississippi State University |
| Detected Language | English |
| Type | text |
| Format | application/pdf |
| Source | Theses and Dissertations |
Page generated in 0.002 seconds